Texture and magnetic properties improvement of a 3% Si non-oriented electrical steel by Sb addition
نویسندگان
چکیده
منابع مشابه
Influence of Antimony on the Texture and Properties of 2 % Si , 0 . 3 % A 1 Steel for Non - Oriented Sheet
The effect of additions of antimony (0.05% Sb) to silicon steel on the improvement of the electrical properties of non-oriented steel sheet was investigated. Measurements of surface segregation of Sb were performed under UHV conditions in the temperature range from 450 to 900 OC, using AES and TDS. Maximum equilibrium surface segregation of antimony was determined at 700 OC. At higher temperatu...
متن کاملThe Effect of Cold Rolling Process on the Microstructure and Texture Evolution in a 1 wt. % Si Non-oriented Electrical Steel
In this study, the effect of cold rolling process on the microstructure and texture evolution in 1wt. % Si non-oriented electrical steel was investigated. For this purpose, all samples were processed through single-stage hot rolling at 1100 ° C and two-stage cold rolling (cross rolling and unidirectional rolling) with intermediate annealing at 650 °C for 35 seconds. Finally, all of them were fu...
متن کاملSecondary recrystallization characteristics of 3%Si grain-oriented electrical steel
A secondary recrystallization Lab study focusing on the secondary recrystallization temperature and magnetic properties was carried out on cold rolling industrial samples of 3%Si grain-oriented electrical steel produced by low slab reheating temperature technology. The results showed a secondary recrystallization temperature, determined by the observed grain size change, of 1080 C with annealin...
متن کاملImprovement of Magnetic Properties and Texture of FePt Thin Films on MgO Substrates by Sn Addition
In this work, we studied the effects of Sn addition on the ordering temperature of FePt thin film. The coercivity of FePtSn film was about 1000 Oe greater than the coercivity of FePt film for an annealing temperature of 600C. Therefore, Sn addition was effective in promoting the L10 ordering and in reducing the ordering temperature of the FePt film. From our X-ray diffraction results, we found ...
متن کاملthe effect of cold rolling process on the microstructure and texture evolution in a 1 wt. % si non-oriented electrical steel
in this study, the effect of cold rolling process on the microstructure and texture evolution in 1wt. % si non-orientedelectrical steel was investigated. for this purpose, all samples were processed through single-stage hot rolling at1100 ° c and two-stage cold rolling (cross rolling and unidirectional rolling) with intermediate annealing at 650 °cfor 35 seconds. finally, all of them were fully...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Magnetism and Magnetic Materials
سال: 2013
ISSN: 0304-8853
DOI: 10.1016/j.jmmm.2012.11.009