Thin films of AgIn5(S/Se)8 prepared in a two stage process
نویسندگان
چکیده
منابع مشابه
AgInSe2 thin films prepared by electrodeposition process
In this work, the one step electrodeposition process was used to prepare Ag-In-Se thin films. The films were deposited at room temperature from a bath containing 1-3x10 M AgNO3, 6x10 -2 M InCl3 and 3x10 -2 M of H2SeO3. The KSCN at a concentration of 0.681 M was used as complexing agent. The pH value of the solution was 1.4. Applied potentials to SCE were chosen between -0.3 V and -1.1 V. Films ...
متن کاملTwo-Stage Chemical Deposition of Oxide Films
Two-stage chemical deposition (TSCD) technique is used to produce ZnO, Mn2O3 and NiO films on soda-lime glass (SL-G) from an aqueous solution of zinc, manganese and nickel complex, respectively. The TSCD method enables the deposition of metal oxide thin films with a thickness which can be controlled during the preparation procedure. The ZnO, Mn2O3 and NiO thin films were polycrystalline films w...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملStructural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films
Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...
متن کاملCharacterization of Ito Thin Films Prepared by Spinning Deposition Starting from a Sol-gel Process
ITO thin films were deposited by spin coating method starting from indium and tin propoxide in the frame of a sol-gel process. Films with the thickness corresponding to 68 nm for one layer deposition were produced and characterized by X-ray diffraction, transmission electron microscopy and infrared reflection spectroscopy. Low conductivity polycrystalline films exhibiting cubical structure (bix...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Science: Materials in Electronics
سال: 2016
ISSN: 0957-4522,1573-482X
DOI: 10.1007/s10854-016-5730-8