failure mechanisms investigation in thermal barrier coatings under isothermal and non-sothermal fatigue loadings using design of experiments

Failure Mechanisms Investigation in Thermal Barrier Coatings under Isothermal and Non-sothermal Fatigue Loadings using Design of Experiments

In this article, failure and fracture mechanisms in an aluminum alloy (which has been used in diesel internal combustion engines), with and without ceramic thermal barrier coatings, have been investigated under isothermal and non-isothermal fatigue loadings. In this research, the base material is an aluminum-silicon-magnesium alloy and the thermal barrier coating includes a metallic bond coat l...

investigation of thermal comfort properties of woven sport fabric using blend of estabragh fibers

امروزه لباس در نظر ورزشکاران و کسانی که برای اوقات فراغت خود و یا برای رسیدن به اندامی متعادل، ورزش می کنند؛ بسیار با اهمیت است. احساس مطلوب از لباس در زمره خصوصیات راحتی پوشش می باشد. خصوصیات انتقال رطوبت لباس، در ارزیابی راحتی حسی و حرارتی منسوجات تولید شده از آن ها بسیار مهم است. هدف از این تحقیق، معرفی پارچه جدید است که متشکل از الیاف استبرق با خواص منحصر به فرد می باشد. استبرق لیف طبیعی تو...

Failure analysis of suspension plasma sprayed thermal barrier coatings

Mechanisms governing the high temperature erosion of thermal barrier coatings

The impact of thermal barrier coatings by hard projectiles at high temperature has been analyzed. Three different domains have been explored: each differentiated by particle size, velocity, temperature and TBC composition. Domain I applies when the projectile creates deeply penetrating plastic/densification zones. In this case, short time elastic effects are relatively unimportant. The response...

AN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS

In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...

Fatigue Failure and Damage Analysis of an Anti-roll Bar Subjected to Fatigue Experiments

The available fatigue theories have been examined using simple specimens subjected to bending or tension-compression loads. Therefore, the stress fields have been generally one or two dimensional. Anti-roll bar is a component belongs to the suspension system of the vehicles. In spite of having simple circular section, due to the having several curvatures, this component experiences a three-dime...