2014 The technique of « monochromatic Laue » X-ray scattering has been used to carry out a comparative study of the different phases of RbAlF4 and KA1F4. In both materials diffuse scattering has been observed. In the former case where displacive transitions occur, the diffuse scattering is surrounding the superlattice Bragg peaks rising below Tc and is well interpreted in the light of the phonon spectrum. In the latter case where the transition is « martensitic », the diffuse scattering is located along diffuse rods and several extra-spots have been observed. The domain arrangement following the martensitic transformation is studied. J. Physique 48 (1987) 625-633 AVRIL 1987,
منابع مشابه
A premartensitic phase in KAlF4: neutron and X-ray scattering evidences
2014 From elastic neutron scattering experiments, it is shown that the anomalies which have been recently observed in the high temperature phase of KAlF4 by the X-ray mono-Laue technique can be attributed to embryonic domains of a premartensitic phase which coherently coexists with the high temperature phase. The arrangement of the domains and the lattice parameters of the premartensitic phase ...
متن کاملClassification of Displacive Transformations : What is a Martensitic Transformation ?
The displacive transformation classification proposed at ICOMAT 79 [I] is reviewed in light of recent progress in mechanistic understanding. Issues considered include distinctions between shuffle transformation vs. self-accommodating shear, dilatation vs. shear-dominant transformation, and nucleated vs. continuous transformation. 1. HISTORICAL INTRODUCTION Cohen, Olson and Clapp (COC) at ICOMAT...
متن کاملStructural aspects of displacive transformations: what can optical microscopy contribute? Dehydration of Sm2(C2O4)3·10H2O as a case study
For martensitic transformations the macroscopic crystal strain is directly related to the corresponding structural rearrangement at the microscopic level. In situ optical microscopy observations of the interface migration and the change in crystal shape during a displacive single crystal to single crystal transformation can contribute significantly to understanding the mechanism of the process ...
متن کاملSurface Hardness Measurment and Microstructural Characterisation of Steel by X-Ray Diffraction Profile Analysis
An X-ray diffraction line will broaden considerably when steels change into martensitic structure on quenching. The results presented in this paper show that X-ray diffraction technique can be employed for a rapid and nondestructive measurement of hardness of hardened steel. Measurement on various quenched and tempered steels showed that the breadth of its diffraction peak increased with increa...
متن کاملAn Investigation on Mechanical Properties of Ultrafine Grained 316 Stainless Steel by Thermomechanical Treatment
In this paper, an advanced thermo-mechanical treatment was conducted on AISI 316 austenitic stainless steel. At first, three samples were rolled at the ambient temperature, the temperature of -20 ºC (dry ice and ethanol) and -196 ºC (liquid nitrogen). Then, the samples were annealed at 800 ºC in the time range of 1 to 15 minutes. In each step, the microhardness values of the samples were measur...