Inhomogenous doping induced nanocrystals imperfect self-assembled to synthesis of porous AgPb10BiTe12 nanosheets and their thermoelectric transport properties
نویسندگان
چکیده
Please note that technical editing may introduce minor changes to the text and/or graphics, which may alter content. The journal’s standard Terms & Conditions and the Ethical guidelines still apply. In no event shall the Royal Society of Chemistry be held responsible for any errors or omissions in this Accepted Manuscript or any consequences arising from the use of any information it contains. Accepted Manuscript ChemComm
منابع مشابه
Bi-functional NaLuF4:Gd3+/Yb3+/Er3+ nanocrystals: hydrothermal synthesis, optical and magnetic properties
Magnetic-fluorescent lanthanide doped sodium lutetium fluoride (NaLuF4:Yb3+/Er3+/Gd3+) nanocrystals were synthesized via facile hydrothermal method by varying concentration of Gd3+. Powder X-ray powder diffraction (PXRD), scanning electron microscopy (SEM),transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS), p...
متن کامل2D Porous ZnO Nanosheets: One Pot Synthesis with Low Turn-on Field
Low turn-on field of 2.3 V/µm was found for the emission current density of 10 µA/cm2 from 2D porous ZnO nanosheets. High current density of 0.76 mA/cm2 was drawn at an applied field of 4.1 V/µm. The observed low turn-on field of porous ZnO nanosheets has been found to be superior to the other ZnO nanostructures reported in the literature. Also, the emission current stability over a period of 3...
متن کاملControlled synthesis of ultrathin lamellar Eu(2)O(3) nanocrystals: self-assembly of 1D nanowires to 2D nanosheets.
By using 1,5-pentanediol as a capping and structure directing agent, ultrathin Eu2O3 nanosheets (<1 nm) have been synthesized and assembled into a layered structure. The lateral dimensions of the nanosheets can be tuned by simply controlling the reaction time. These layered structures exhibit a strong quantum size effect due to the extremely small thickness of the assembled nanosheets.
متن کاملخواص ترابردی و شبه گاف در ابررسانای NdBa2-xLax Cu3O7-δ
Polycrystalline samples of NdBa2-xLaxCu3O7-δ with x=0, 0.05, 0.10, 0.15, 0.20, and 0.30 were made by standard solid state methods. The transport and superconducting properties have been studied by the resistivity measurements as a function of temperature and doping concentration. In order to measurements the hole concentration in CuO2 planes, the room temperature thermoelectric power was measu...
متن کاملتأثیر آلاینده خنثای Ca-La بر روی خواص ترابردی و ابررسانایی ترکیب 123-Nd
Polycrystalline samples of Nd1-xCaxBa2-xLaxCu3O7-δ (with 0.0 ≤ x ≤ 0.15) were prepared by the standard solid state method. The transport and superconducting properties have been studied by the resistivity and thermoelectric power measurements as a function of temperature and doping concentration. With increasing doping concentration, the resistivity was increased and thermoelectric power was c...