Effects of CuZnAl Particles on Properties and Microstructure of Sn-58Bi Solder
نویسندگان
چکیده
With the purpose of improving the properties of the Sn-58Bi lead-free solder, micro-CuZnAl particles ranging from 0 to 0.4 wt % were added into the low temperature eutectic Sn-58Bi lead-free solder. After the experimental testing of micro-CuZnAl particles on the properties and microstructure of the Sn-58Bi solders, it was found that the wettability of the Sn-58Bi solders was obviously improved with addition of CuZnAl particles. When the addition of CuZnAl particles was 0.2 wt %, the wettability of the Sn-58Bi solder performed best. At the same time, excessive addition of CuZnAl particles led to poor wettability. However, the results showed that CuZnAl particles changed the melting point of the Sn-58Bi solder slightly. The microstructure of the Sn-58Bi solder was refined by adding CuZnAl particles. When the content of CuZnAl addition was between 0.1 and 0.2 wt %, the refinement was great. In addition, the interfacial IMC layer between new composite solder and Cu substrate was thinner than that between the Sn-58Bi solder and Cu substrate.
منابع مشابه
Interfacial Reaction and Mechanical Properties of Sn-Bi Solder joints
Sn-Bi solder with different Bi content can realize a low-to-medium-to-high soldering process. To obtain the effect of Bi content in Sn-Bi solder on the microstructure of solder, interfacial behaviors in solder joints with Cu and the joints strength, five Sn-Bi solders including Sn-5Bi and Sn-15Bi solid solution, Sn-30Bi and Sn-45Bi hypoeutectic and Sn-58Bi eutectic were selected in this work. T...
متن کاملInterfacial Reactions Between Sn–58 mass%Bi Eutectic Solder and (Cu, Electroless Ni–P/Cu) Substrate
The growth kinetics of intermetallic compound layers formed between eutectic Sn–58Bi solder and (Cu, electroless Ni–P/Cu) substrate were investigated at temperature between 70 and 120◦C for 1 to 60 days. The layer growth of intermetallic compound in the couple of the Sn–58Bi/Cu and Sn–58Bi/electroless Ni–P system satisfied the parabolic law at given temperature range. As a whole, because the va...
متن کاملInvestigation of microstructure and physical properties in nanocomposite solder reinforced with various percent of graphene nanosheets (SAC0307+GNSs)
Development of electronic industries, compression of electronic equipment, and removing lead from electronic circuits for environmental issues, resulted in a significant challenge in design and development of tin-based lead-free solders with physical and mechanical properties similar to old tin-lead alloys. In this regard, the set of Sn-Ag-Cu alloys with eutectic and near eutectic compositions ...
متن کاملInvestigation of microstructure and physical properties in nanocomposite solder reinforced with various percent of graphene nanosheets (SAC0307+GNSs)
Development of electronic industries, compression of electronic equipment, and removing lead from electronic circuits for environmental issues, resulted in a significant challenge in design and development of tin-based lead-free solders with physical and mechanical properties similar to old tin-lead alloys. In this regard, the set of Sn-Ag-Cu alloys with eutectic and near eutectic compositions ...
متن کاملInfluence of Ag micro-particle additions on the microstructure, hardness and tensile properties of Sn-9Zn binary eutectic solder alloy
In this study, an addition of Ag micro-particles (8–10 lm) with a content in the range between 0 and 1.5 wt.% to Sn–9Zn eutectic solder, were examined in order to understand the effect of Ag additions as the particulate reinforcement on the microstructural and mechanical properties as well as the thermal behavior of the newly developed composite solders. Here, an approach to prepare a micro-com...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 10 شماره
صفحات -
تاریخ انتشار 2017