Dissolution and Precipitation Behaviour during Continuous Heating of Al–Mg–Si Alloys in a Wide Range of Heating Rates
نویسندگان
چکیده
In the present study, the dissolution and precipitation behaviour of four different aluminium alloys (EN AW-6005A, EN AW-6082, EN AW-6016, and EN AW-6181) in four different initial heat treatment conditions (T4, T6, overaged, and soft annealed) was investigated during heating in a wide dynamic range. Differential scanning calorimetry (DSC) was used to record heating curves between 20 and 600 °C. Heating rates were studied from 0.01 K/s to 5 K/s. We paid particular attention to control baseline stability, generating flat baselines and allowing accurate quantitative evaluation of the resulting DSC curves. As the heating rate increases, the individual dissolution and precipitation reactions shift to higher temperatures. The reactions during heating are significantly superimposed and partially run simultaneously. In addition, precipitation and dissolution reactions are increasingly suppressed as the heating rate increases, whereby exothermic precipitation reactions are suppressed earlier than endothermic dissolution reactions. Integrating the heating curves allowed the enthalpy levels of the different initial microstructural conditions to be quantified. Referring to time–temperature–austenitisation diagrams for steels, continuous heating dissolution diagrams for aluminium alloys were constructed to summarise the results in graphical form. These diagrams may support process optimisation in heat treatment shops. OPEN ACCESS Materials 2015, 8 2831
منابع مشابه
Fluidized Bed Heat Treatment of Cast Al-Si-Cu-Mg Alloys
The effects of fluidized bed heat treatment on the microstructural and mechanical properties of Al-Si-Cu-Mg cast alloys, namely,3 54 and 319, were studied. The heating rate in fluidized beds (FBs) is greater vis-a`-vis conventional electrical resistancef urnaces (CFs). The high heating ratei nF Bs increases the kinetics of metallurgical phenomena such as Si fragmentation and spherodization duri...
متن کاملTHERMAL ANALYSIS AND KINETICS OF THE PRECIPITATION IN WROUGHT Al-Mg, Al-Mg-ScAND Al-Mg-Sc-Me (Me=Zr, Ti) ALLOYS
Precipitation behaviour of wrought Al-6Mg alloys with ternary scandium and quaternary zirconium and titanium has been studied. Hardness measurements and resistivity studies are employed to assess the precipitation behaviour of scandium doped Al-6Mg alloy without or with quaternary additions of zirconium and titanium. Further, the kinetics of precipitations are studied by differential scanning c...
متن کاملLocalized Recrystallization in Cast Al-Si-Mg Alloy During Solution Heat Treatment: Dilatometric and Calorimetric Studies
During heat treatment, the work piece experiences a range of heating rates depending upon the sizes and types of furnace. When the Al-Si-Mg cast alloy is heated to the solutionizing temperature , recrystallization takes place during the ramp-up stage. The effect of heating rate on recrystallization in the A356 (Al-Si-Mg) alloy was studied using dilatometric and calorimetric methods. Recrystalli...
متن کاملEvolution of microstructure and precipitation in heat-treatable aluminium alloys during ECA pressing and subsequent heat treatment
The precipitation and evolution of microstructure in a spray-cast Al-7034 alloy and a commercial wrought Al-2024 alloy were studied after equal-channel angular pressing (ECAP) using transmission electron microscopy and differential scanning calorimetry (DSC). Microstructural examination showed the grain sizes of both alloys were reduced to the range of ~0.3–0.5 μm through ECAP. The DSC analysis...
متن کاملEFFECT OF HEAT TREATMENT AND ALLOYING ELEMENTS ON PRECIPITATION AND SURFACE BEHAVIOR OF Co-Cr-Mo ALLOYS
The microstructures of as-cast and heat-treated Co-Cr-Mo with addition of C, Si and Mn have been investigated with a focus on phase and dissolution of precipitates. The heat treatment temperatures and heating periods employed ranged from 1448 to 1548 K and 0 to 43.2 ks, respectively. The precipitates observed in the as-cast and heat-treated alloys were carbides (M23C6, eta-phase, and pi-phase) ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 8 شماره
صفحات -
تاریخ انتشار 2015