Degradation mechanism of phosphorescent-dye-doped polymer light-emitting diodes
نویسندگان
چکیده
The degradation mechanism of phosphorescent-dye-doped polymer light-emitting diodes ~PLEDs! is investigated. The active medium of our PLED is a polymer blend comprising poly~vinylcarbazole! ~PVK!, @2-~4-biphenylyl!-5-~4-tert-butyl-phenyl!-1,3,4-oxadiazole# ~t-PBD!, and platinum~II!-2,8,12,17-tetraethyl-3,7,13,18-tetramethylporphyrin ~PtOX!. The cyclic voltammetry result shows that the reductive reversibility of PtOX is poor. This result suggests that PLED doped with PtOX is not stable if PtOXs trap electrons and turn into anionic PtOX species. This was indeed verified by fabricating single-layer PLEDs with various amounts of electron-transporting material, t-PBD. A slower degradation rate was observed from the devices with higher concentration of t-PBD, because of the reduction of the electron accumulation at the PtOX sites. The half decay lifetime of our phosphorescent polymer LED has been improved by a factor of ;40, from 1.2 to 45 h. © 2001 American Institute of Physics. @DOI: 10.1063/1.1404995#
منابع مشابه
High-efficiency organic polymer light-emitting heterostructure devices on flexible plastic substrates
Articles you may be interested in High-contrast organic light-emitting diodes on flexible substrates Appl. High-performance polymer light-emitting diodes doped with a red phosphorescent iridium complex Appl. High-efficiency, low-drive-voltage, semitransparent stacked organic light-emitting device Appl.
متن کاملEnergy transfer and device performance in phosphorescent dye doped polymer light emitting diodes
Singlet and triplet–triplet energy transfer in phosphorescent dye doped polymer light emitting devices were investigated. Poly(N-vinylcarbazol) and poly@9,98-di-n-hexyl-2,7-fluorene-alt1,4-(2,5-di-n-hexyloxy)phenylene] ~PFHP! were selected as the host polymer for the phosphorescent dopants fac-tris~2-phenylpyridine! iridium~III! @Ir(ppy)3# and 2,3,7,8,12,13, 17,18-octaethyl-21H,23H-porphyrin pl...
متن کاملPhosphorescent Molecularly Doped Light-Emitting Diodes with Blended Polymer Host and Wide Emission Spectra
Stable green light emission and high efficiency organic devices with three polymer layers were fabricated using bis[2-(4'-tert-butylphenyl)-1-phenyl-1H-benzoimidazole-N,C²'] iridium(III) (acetylacetonate) doped in blended host materials. The 1 wt% doping concentration showed maximum luminance of 7841 cd/cm² at 25.6 V and maximum current efficiency of 9.95 cd/A at 17.2 V. The electroluminescence...
متن کاملOn the origin of the redshift in the emission wavelength of InGaN/GaN blue light emitting diodes grown with a higher temperature interlayer
Related Articles Multilayered graphene anode for blue phosphorescent organic light emitting diodes Appl. Phys. Lett. 100, 133304 (2012) Multilayered graphene anode for blue phosphorescent organic light emitting diodes APL: Org. Electron. Photonics 5, 82 (2012) Electroluminescence from strained germanium membranes and implications for an efficient Si-compatible laser Appl. Phys. Lett. 100, 13111...
متن کاملGraded-host phosphorescent light-emitting diodes with high efficiency and reduced roll-off
Related Articles Encapsulating light-emitting electrochemical cells for improved performance Appl. Phys. Lett. 100, 193508 (2012) Efficiency degradation behaviors of current/thermal co-stressed GaN-based blue light emitting diodes with vertical-structure J. Appl. Phys. 111, 093110 (2012) Influence of laser lift-off on optical and structural properties of InGaN/GaN vertical blue light emitting d...
متن کامل