Low-temperature growth of carbon nanotubes by selective heating of catalyst
نویسندگان
چکیده
Currently, high crystalline quality materials such as carbon nanotubes (CNTs) are produced only at a temperature in an excess of 500 C. This paper reports on low-temperature synthesis of CNTs by selective heating of catalytic particles using two complementary mechanisms: enhanced exothermic catalytic reactions and inductive heating by radio frequency electromagnetic fields.
منابع مشابه
A PARAMETRIC STUDY ON THE GROWTH OF SINGLE-WALLED CARBON NANOTUBES OVER CO-MO/MGO NANOCATALYST IN A FLUIDIZED BED REACTOR BY CCVD METHOD
Single-walled carbon nanotubes (SWNTs) with high yield and quality were synthesized using chemical vapor deposition (CVD) over Co-Mo/ MgO nanocatalyst in a fluidized bed reactor. Different parameters such as temperature, the ratio of hydrocarbon source to hydrogen, the flow rate of gas, growth time, the size of catalyst particles, heating rate, and the kind of hydrocarbon source were examined t...
متن کاملGrowth of CNTs over Fe–Co/Nanometric TiO2 Catalyst by CVD: The Effects of Catalyst Composition and Growth Temperature
In this research carbon nanotubes were produced by chemical vapor deposition of acetylene over a mixture of iron and cobalt catalysts supported on nanometric TiO2 and the influences of two synthesis parameters: growth temperature and catalyst composition ratio on properties of end-product carbon nanotubes were investigated. The catalytic basis was prepared by wet impregnation ...
متن کاملReactor Design for Low-Temperature Growth of Vertically Aligned Carbon Nanotubes
This paper reports on the design of novel reactor for low-temperature growth of Vertically Aligned Carbon Nanotubes (VACNTs). Two mechanisms for selective heating catalytic nanoparticles were investigated: (i) a heating from exothermic reaction of catalytic oxidation and (ii) an induction heating. The requirements for efficient induction heating catalytic particles of size varying from micron t...
متن کاملEvaluation of catalyst ball-milling process on growth and diameter of carbon nanotubes on iron nanoparticles
In this study, we describe the growth of carbon nanotubes on commercial iron nanoparticles without carbon shell (Fe (nm), size 2O3 and Fe* (nm)/MgO) was carried out by mixing commercial Fe* nanoparticles (as catalyst) with Al2O3 and MgO powders (as supports)by using ball-milling method. The results show in spite of the fact that ball-milling process can have neg...
متن کاملEvaluation of catalyst ball-milling process on growth and diameter of carbon nanotubes on iron nanoparticles
In this study, we describe the growth of carbon nanotubes on commercial iron nanoparticles without carbon shell (Fe (nm), size 2O3 and Fe* (nm)/MgO) was carried out by mixing commercial Fe* nanoparticles (as catalyst) with Al2O3 and MgO powders (as supports)by using ball-milling method. The results show in spite of the fact that ball-milling process can have neg...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2007