اثر دمای کلسینه بر خواص ساختاری نانوذرات ZrO2 تهیه شده به روش سل ژل اصلاح شده در محیط ژلاتین

Authors

  • خرسند زاک, علی آموزش عالی فنی و مهندسی اسفراین
  • خرمی, غلامحسین دانشگاه فردوسی مشهد
  • نوری, محبوبه سادات دانشگاه فردوسی مشهد
  • کمپانی, احمد دانشگاه فردوسی مشهد
Abstract:

In this research, ZrO2 nanoparticles were synthesized by modified sol-gelmethod at different calcination temperatures (600, 800, 1000, 1200 °C).  Zirconium (IV) oxynitrate hydrate as zirconium source, gelatin as polymerization and stabilizer agent and distilled water was used as the solvent. The crystal structures of the synthesized samples were characterized by X-ray diffraction (XRD) and the average crystallite size was estimated by Scherrer fomula and Williamson-Hall method. Transmission electron microscopy (TEM) images showed that the average particle size of zirconia calcined at 600 and 1200°C are 10 and 32 nm, respectively. FTIR analysis in the range of 400-4000 cm-1 was  carried out, the results of FTIR showed that the samples are calcined at 600 and 1200 °C have tetragonal and monoclinc structure, respectively. FT-IR spectroscopy analyses of the synthesized samples confirmed the XRD results.  

Upgrade to premium to download articles

Sign up to access the full text

Already have an account?login

similar resources

اثر دمای کلسینه بر خواص ساختاری نانوذرات zro۲ تهیه شده به روش سل ژل اصلاح شده در محیط ژلاتین

در این پژوهش، نانوذرات zro2 (زیرکونیا) به روش سل ژل اصلاح شده در دماهای 600، 800، 1000 و 1200 درجه­ی سانتی گراد سنتز شدند. اکسی نیترات زیرکونیوم به عنوان تامین کننده زیرکونیوم، ژلاتین به منظور عامل پلیمریزاسیون و پایدار کننده و نیز آب مقطر به عنوان حلال مورد استفاده قرار گرفتند. ساختار بلوری پودرها به روش پراش پرتو ایکس (xrd) مورد بررسی قرار گرفت و اندازه­ی میانگین بلورک ها با استفاده از فرمول ...

full text

ساخت و بررسی خواص ساختاری نانوکاتالیست‌های NiO/MgO تهیه شده به روش سل-ژل اصلاح شده

اکسید نیکل بر پایه اکسید منیزیا به عنوان کاتالیست و در فرآیندهای ریفرمینگ متان برای تولید گاز سنتزی، کاربردهای فراوانی در صنایع شیمیایی و متالورژیکی دارد. در این تحقیق نانوکریستال‌های NiO/MgO با درصدهای مختلف نیکل (10 و 15 درصد وزنی) و با استفاده از روش سل-ژل اصلاح شده تهیه شدند. عملیات حرارتی کلسیناسیون پیش ماده‌ها بعد از بدست آمدن ژل پلیمری در دماهای °C 700 و 800 و به مدت 4 ساعت انجام گردید. ...

full text

اثر بربرین در تنظیم آستروسیتهای Gfap+ ناحیه هیپوکمپ موشهای صحرایی دیابتی شده با استرپتوزوتوسین

Background: Diabetes mellitus increases the risk of central nervous system (CNS) disorders such as stroke, seizures, dementia, and cognitive impairment. Berberine, a natural isoquinolne alkaloid, is reported to exhibit beneficial effect in various neurodegenerative and neuropsychiatric disorders. Moreover astrocytes are proving critical for normal CNS function, and alterations in their activity...

full text

اثر بربرین در تنظیم آستروسیتهای Gfap+ ناحیه هیپوکمپ موشهای صحرایی دیابتی شده با استرپتوزوتوسین

Background: Diabetes mellitus increases the risk of central nervous system (CNS) disorders such as stroke, seizures, dementia, and cognitive impairment. Berberine, a natural isoquinolne alkaloid, is reported to exhibit beneficial effect in various neurodegenerative and neuropsychiatric disorders. Moreover astrocytes are proving critical for normal CNS function, and alterations in their activity...

full text

بررسی تاثیر مقدار ژلاتین بر ویژگی ساختاری نانوپودر پیزوالکتریک بدون سرب (K0.5Na0.5)NbO3 تهیه شده به روش سل ژل اصلاح شده در محیط ژلاتین

In this research, lead-free piezoelectric Sodium potassium niobate nanopowders (K0.5Na0.5)NbO3 were synthesized using a modified sol–gel method. Nitrate sodium, nitrate potassium, and ammonium niobate oxalate were used as starting materials. Gelatin which is natural polymer was used as polymerization agent and distilled water was used as solvent. The crystal structure of the prepared powders is...

full text

تأثیر pH بر خواص ساختاری و مغناطیسی نانوذرات PbFe12O19 ساخته شده به روش سل- ژل

In this research, lead hexaferrites nanoparticles (PbFe12O19) were prepared by sol-gel method. The effect of pH on the structural and magnetic properties of PbFe12O19 was studied. The attempt in this paper was to depict the effect of change in sol-gel pH on the size and morphology of the samples as well as their structural and magnetic properties. Therefore, samples with pH = 1.8, 3, 5, 6, 7, a...

full text

My Resources

Save resource for easier access later

Save to my library Already added to my library

{@ msg_add @}


Journal title

volume 24  issue 4

pages  779- 788

publication date 2017-01

By following a journal you will be notified via email when a new issue of this journal is published.

Keywords

No Keywords

Hosted on Doprax cloud platform doprax.com

copyright © 2015-2023