خواص مغناطیسی بلوری آلیاژ نانوذرات آهن- پلاتین (L10-FePt) در گذار فاز
نویسنده
چکیده مقاله:
High magneto- crystalline anisotropy (ku=7×106j/m3) of L10-FePt nanoparticles are an excellent candidate for ultra high-density magnetic recording. The 4 nm FePt nanocrystals were prepared by superhydride reduction of FeCl2·4H2O and Pt(acac)2 precursors in the phenyl ether by reduction of the 1, 2-hexadecanediol and LiBEt3H superhydride. The crystal and magnetic structures were studied by XRD and VSM analysis. By TEM and EDS analyses the size distribution and molar concentration of Fe/Pt of the nanoparticles were determined. The results showed that the particles are first superparamagnetic before heat treatment and then a phase transition accrue from disorder fcc to order fct structure after annealing. Finally, the phase transition leads the magnetic anisotropy of hard FePt nanoparticles to increase to 7 kOe.
منابع مشابه
مطالعۀ گذار فاز هماتیت-آهن در فرآیند تولید نانوذرات هسته-پوستۀ آهن-کربن و بررسی خواص مغناطیسی و الکترومغناطیسی آن‌ها
The structural properties and microwave absorption capability of the iron nanoparticles and iron-carbon core-shell nanoparticles have been studied, in the present paper. The investigated nanoparticles were synthesized by hydrothermal route and by reduction of hematite nanoparticles during annealing in argon-hydrogen atmosphere. Hematite-iron phase transformation during the reduction process has...
متن کاملالکتروانباشت و مطالعه ساختاری و خواص مغناطیسی نانوساختارهای آهن-پلاتین
در این تحقیق الکتروانباشت تک حمام لایه‌های نازک فلزی Pt و آلیاژی FePt با درصدهای مختلف آهن، بر روی زیرلایه-های مس و طلا، مطالعه گردید. الکتروانباشت در مد کرنوکولومتری (CHC) تحت پتانسیل صورت گرفت. با استفاده از ولتامتری چرخه‌ای (CV) ولتاژ شروع انباشت لایه‌های آلیاژی مشخص شد. در ادامه بس لایه‌ای‌های FePt/Pt با ضخامت-های متفاوت لایه‌های پلاتین بر زیر لایه‌های مس و طلا رسوب داده شد و تأثیر این تغیی...
متن کاملStructural studies of L10 FePt nanoparticles
We have studied the lattice parameter changes of L10 FePt nanoparticles annealed to near equilibrium as a function of composition by x-ray diffraction. We have found that the ~111! diffraction peak shifts linearly with composition, however, the c parameter mostly changes in the Pt rich compositions and the a parameter mostly changes in the Fe rich compositions with respect to the equiatomic com...
متن کاملElectrodeposition of coercive L10 FePt magnets
This is a PDF file of an unedited manuscript that has been accepted for publication. As a service to our customers we are providing this early version of the manuscript. The manuscript will undergo copyediting, typesetting, and review of the resulting galley proof before it is published in its final citable form. Please note that during the production process errors may be discovered which coul...
متن کاملتأثیر دمای بازپخت بر خواص ساختاری و مغناطیسی لایه نازک آهن-پلاتین
هدف اصلی این تحقیق، بررسی خواص ساختاری و مغناطیسی لایه نازک FePt نسبت به دمای بازپخت است. لایه‌های نازک FePt به روش کندوپاش روی زیرلایه شیشه ای با نرخ 6 و با توان W 110 رسوب داده شدند. خلأ اولیه محفظه کندوپاش برابر Torr 7-10 5 و فشار گاز آرگون mTorr 3 در نظر گرفته شد. پس از تهیه نمونه‌ها، در محدوده 650-450 به مدت 30 دقیقه بازپخت شدند. شناسایی فازی لایه نازک ب...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 16 شماره 1
صفحات 1- 5
تاریخ انتشار 2016-06
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023