Air Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading
نویسندگان
چکیده مقاله:
An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specimens, after loading were investigated using Field Emission Scanning Electron Microscopy (FE-SEM). Results showed in spite of forming various oxide layers within the BC its oxidation in Bond Coat/Top Coat interface behave the same as samples coated by other methods and no failure was observed at substrate/BC interface or within the BC.
منابع مشابه
Thermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
The effects of the bond coat species on the delamination or fracture behavior in thermal barrier coatings (TBCs) was investigated using the yclic thermal fatigue and thermal-shock tests. The interface microstructures of each TBC showed a good condition without cracking or delamination after flame thermal fatigue (FTF) for 1429 cycles. The TBC with the bond coat prepared by the air-plasma spray ...
متن کاملThermal Stress Resistance to Fracture and its Relation to with Resistance to Thermal Fatigue and Shock
Dense Silicon nitride was investigated to determine the effect of its microstructural parameters and densification on thermo-mechanical properties and thermal stress resistance to fracture initiation during a hot or cold mechanical and thermal shock testing. The different materials and microstructures were obtained by changing the parameters such as the type of the powder, additive, forming p...
متن کاملThermal Stress Resistance to Fracture and its Relation to with Resistance to Thermal Fatigue and Shock
Dense Silicon nitride was investigated to determine the effect of its microstructural parameters and densification on thermo-mechanical properties and thermal stress resistance to fracture initiation during a hot or cold mechanical and thermal shock testing. The different materials and microstructures were obtained by changing the parameters such as the type of the powder, additive, forming p...
متن کاملSynthesis and Characterization of Mechanical Behavior and Thermal Shock Resistance of Macro-Porous SiC Solar Absorber
The concentrated solar power (CSP) is one of the renewable energy sources in which solar irradiation heat energy will be used in a steam turbine to generate electrical grid. Solar radiation is absorbed by a solar receiver reactor on the surface of a porous solar absorber. In this survey, synthesis and mechanical/thermal characterization of micro-porous silicon carbide (SiC) absorber to be used ...
متن کاملEffect of Surface Morphologies on the Isothermal Oxidation Behavior of MCrAlY Coatings Fabricated by High-velocity Oxyfuel Processes
In this study, the effect of surface morphologies on the isothermal oxidation behavior of MCrAlY coatings fabricated by high-velocity oxyfuel (HVOF) processes was investigated. To do so, free standing coatings with as-sprayed and polished surfaces were isothermally oxidized at 1050°C. The thickness of the bond coat was approximately 380μm. The Ra of the as-sprayed and polished surfaces were 6.4...
متن کاملpetrology and geochemistry of khar-bash (western shahrood) and its relation ship to iron mineralization
منطقه مورد مطالعه در 23 کیلومتری جنوب غرب شهرستاشاهرود قرار دارد که در نقشه 100000/1 شاهرود قرار گرفته است.ناحیه مورد مطالعه در تقسیمات ساختاری ایران بخشی از زون البرز شرقی است . در طی سنوزوئیک این زون به شدت تحت تأثیر فازهای کوهزایی آلپی قرار گرفته و فعالیت های آتشفشانی انوسن در قسمت های غربی آن دیده می شود . از نظر ترکیب سنگ شناسی منطقه مورد مطالعه متنوع و بیشتر شامل سنگ های رسوبی مانند : آ...
15 صفحه اولمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 32 شماره 6
صفحات 872- 876
تاریخ انتشار 2019-06-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023