Copper Manganese Spinel Coating on a Ferritic Stainless Steel for SOFC Application
نویسنده
چکیده مقاله:
Nowadays, Because of daily reduction of fossil fuels and environmental problems caused by using them, Fuel Cells attracted a major attention as clean and efficient way of generating electrical power. Solid Oxide Fuel Cells (SOFCs) have many advantages to other fuel cell types. High working temperature of SOFCs caused serious challenges including high oxidation rate of interconnects, Spallation and cracks in oxide scale due to mismatch of Thermal Expansion Coefficient (TEC), Cathodic Poisoning and high Area Specific Resistance (ASR) of oxide scale. Manganese containing coatings have overcome these challenges successfully, having unique properties. The purpose of this project is, coating AISI-430 ferritic stainless steel with Cu-Mn Spinel for using as SOFCs interconnects. The coating was done, using Electrophoretic codeposition of CuO and MnO2 with subsequential oxidating thermal treatment for spinel synthesis. Thermal treatment for spinel synthesis was done in 40 hours at 750°C. Phase analysis and microscopic evaluation of coatings showed that Cu-Mn spinel synthesis was done successfully.
منابع مشابه
Development and application of HVOF sprayed spinel protective coating for SOFC interconnects
متن کامل
A review on nanostructured stainless steel implants for biomedical application
Over the last two decades, many researchers have developed a variety of stainless steel-based medical implant types,taking full advantage of nanostructuring technologies. In this paper the application, fabrication and development of nanostructured stainless steel based materials with new composition for medical implants will be discussed. It is well established that application of severe plasti...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملPrecipitation sequence in niobium-alloyed ferritic stainless steel
Niobium is an important alloying element in the design of heat-resistant ferritic stainless steels for automotive exhaust systems. When in solid solution, it improves both the high temperature strength and the resistance to thermal fatigue. However, it also forms several kinds of precipitates during service. These reactions have been modelled, taking into account the multicomponent nature of th...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 9 شماره None
صفحات 57- 69
تاریخ انتشار 2020-05
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023