Developing Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing
نویسنده
چکیده مقاله:
The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ultimate strength of 1960 MPa for austenitizing at 910 ˚C and isothermally transforming to pearlite at 510 ˚C.
منابع مشابه
developing very fine nanopearlitic structure in a high carbon steel wire before drawing
the effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. in this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. the results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملThe Influence of Drawing Speed on Structure Changes in High Carbon Steel Wires
M. Suliga, R. Kruzel, T. Garstka, Czestochowa University of Technology, Czestochowa, Poland J. Gazdowicz Institute of Ferrous Metallurgy Gliwice, Poland In the paper the influence of the drawing speed on structure changes has been assessed. The Scanning Electron Microscope investigation confirmed that for wires drawn with high total draft, exceeding 80 %, makes it impossible to clearly assess t...
متن کاملCarbon dioxide concentrations are very high in developing oilseeds.
A new method has been developed to rapidly determine the total inorganic carbon concentration (gaseous [CO2] + aqueous [CO(2)] + [HCO3-] + [CO3(2)-]) in developing seeds. Seeds are rapidly dissected and homogenized in 1 N HCl in gas-tight vials. The headspace gas is then analyzed by infrared gas analysis. Developing rapeseed (Brassica napus L.) and soybean [Glycine max (L.) Merr.] seeds were an...
متن کاملStatic Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملRecrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...
متن کاملProgressive Changes in the Microstructure and Texture in Pearlitic Steel during Wire Drawing
The evolution of microstructure and texture during wire drawing of pearlitic steel was studied using scanning electron microscopy and X-ray diffraction. Wire drawing induces elongation of ferrite grains with the development of <110> fibre texture. The cementite lamellae also have a tendency to reorient themselves along the wire axis with increasing strain. Viscoplastic self-consistent simulatio...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 8 شماره 2
صفحات 1- 4
تاریخ انتشار 2011-07-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023