Effects of Homogenization Conditions and Hot Rolling Parameters on Grain Refinement of an As-Cast 301 Stainless Steel

نویسندگان

  • A. Kermanpur Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
  • A. Najafizadeh Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
  • M. Eskandari Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
  • M. Karimi Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran
چکیده مقاله:

 In this work, effects of homogenization time of 3 to 13 h at 1200 °C on the grain refinement of as-cast AISI 301 stainless steel after different hot rolling conditions were investigated. The results showed that the minimum grain size of 16±7 mm was achieved when homogenization took place at 1200 °C for 9 h followed by hot rolling at temperature range of 1000–1200 °C with strain of 0.8 and strain rate of 1.2 s-1 and annealing at 1050 °C for 3 min. Effect of Nb element on the retardation of recrystallization was pronounced. It seems that there is an optimum solute segregation below which retardation and above which grain growth of recrystallized grains is dominant. It was also found that this optimum homogenization condition was dependent upon the hot rolling parameters; higher the strain and strain rate resulted in lower homogenizing time at 1200 °C.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

effects of homogenization conditions and hot rolling parameters on grain refinement of an as-cast 301 stainless steel

in this work, effects of homogenization time of 3 to 13 h at 1200 °c on the grain refinement of as-cast aisi 301 stainless steel after different hot rolling conditions were investigated. the results showed that the minimum grain size of 16±7 mm was achieved when homogenization took place at 1200 °c for 9 h followed by hot rolling at temperature range of 1000–1200 °c with strain of 0.8 and strai...

متن کامل

The Effect of Hot Deformation Parameters on Grain Size Refinement in a Martensitic Stainless Steel

The grain size refinement of AISI 422 martensitic stainless steel in the temperature range of 950-1150 ºC was investigated by hot deformation tests. The deformed specimens were held at deformation temperature with delay times of 5 to 300s after achieving a strain of 0.3. The austenite grains exhibit a considerable growth at temperature higher than 1050˚C, while the grain coarsening is negligibl...

متن کامل

Magnificent Grain Refinement of Al-Mg2Si Composite by Hot Rolling

The effect of chemical composition and the hot rolling operations on the microstructure and mechanical properties of in situ aluminum matrix composite with Mg2Si phase as the reinforcement was studied. It was revealed that the modification by phosphorous results in the rounder (more spherical) primary and secondary (eutectic) magnesium silicide intermetallics. During hot rolling, the primary pa...

متن کامل

Strain-Induced Martensite Transformation Simulations during Cold Rolling of AISI 301 Austenitic Stainless Steel

Austenite is a semi-stable phase in most stainless steels that deforms to martensite under Md30 and forms martensitetype ά and ε due to the deformation in the steels. Since the distribution of strain induced martensite plays animportant role in achieving desired properties, the main objective of the present work is to model martensitedistribution of ά during cold rolling using...

متن کامل

the effects of planning on accuracy and complexity of iranian efl students’ written narrative task performance

this study compared the different effects of form-focused guided planning vs. meaning-focused guided planning on iranian pre-intermediate students’ task performance. the study lasted for three weeks and concentrated on eight english structures. forty five pre-intermediate iranian students were randomly assigned to three groups of guided planning focus-on-form group (gpfg), guided planning focus...

15 صفحه اول

Grain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel

In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 5  شماره 2

صفحات  21- 28

تاریخ انتشار 2008-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023