Failure Procedure in Adhesive Composite Joints under Different Types of Loading
نویسندگان
چکیده مقاله:
In this paper, we have used numerical simulation to study failure of adhesive joints in composite plates. To determine the failure load, adhesive joints are subjected to different types of loading and gradual failure of the joint is studied using the finite element method. The composite material failure theory is implemented into the FEM software. Also different geometries for the joint edge are considered and effect of these geometries and fillet chamfer angle on the failure load are investigated.
منابع مشابه
Damage Evolution in Composite Bonded Joints under Fatigue Loading
The fatigue behaviour of single lap bonded joints under fatigue loading was already investigated and a suitable life prediction model was presented and validated [1-2]. The model is based on the actual damage evolution under fatigue load: a crack initiation followed by its propagation up to a critical length [2, 3]. In the present paper the evolution of fatigue damage in single lap joints is ex...
متن کاملFatigue behaviour of composite adhesive lap joints
This paper is concerned with a fatigue study of composite adhesive lap joints produced from a bi-directional woven E-glass fibres and polypropylene. The adhesive used was a Bostik 7452 (Rubber & Plastics Grade) ethyl cyanoacrylate type. The effects of layer orientation, lap joint length and water immersion on the fatigue behaviour were studied. The specimens were immersed in water during period...
متن کاملFailure of Fibrous Composite Plates under Static Biaxial Planar Loading
This paper outlines an experimental investigation carried out for the analysis of failure mechanisms in fibrous laminated composite plates containing stress raisers, in the form of cutouts, under static biaxial planar compressive loadiing. A specially designed biaxial loadiing frame was used to test a series of 48 ply graphite/epoxy composite laminated plates with centrally located circular hol...
متن کاملnon-linear analysis of adhesive joints in composite structures
this paper presents a novel formulation and numerical solutions for adhesively bonded composite joints with non-linear (softening) adhesive behaviour. the presented approach has the capability of choosing arbitrary loadings and boundary conditions. in this model adherends are orthotropic laminates that obey classical lamination theory. the stacking sequences can be either symmetric or asymmetri...
متن کاملMicroleakage comparison of three types of adhesive systems versus GIC-based adhesive in class V composite restorations
Background and aims: New dentin bonding agents and techniques have been developed to reduce microleakage and create higher bond strength. This in-vitro study compared the microleakage of three resin-based adhesives versus a GIC-based adhesive on class V composite restorations. Materials and Methods: Class V cavities were prepared on the buccal surfaces of 72 sound premolars, randomly assigned ...
متن کاملInteraction of laminate damage and adhesive disbonding in composite scarf joints subjected to combined in-plane loading and impact
Impact tests were carried out on composite laminates and composite scarf repairs, while both were subjected to in-plane loading with tensile pre-strain levels up to 5000 microstrain. The results show that pre-straining of the composite laminates has no noticeable influence on the size of the delamination area for the given impact energy of 8 J, which represents a typical barely-visible impact o...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 5 شماره 4
صفحات 647- 651
تاریخ انتشار 2019-06-01
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023