Inverse Co-precipitation Synthesis of Copper Chromite Nanoparticles

نویسندگان

  • Ali Reza Zarei Department of Chemistry, Malek Ashtar University of Technology, P.O. Box: 15875-1774 Tehran, I.R. IRAN
  • Hassan Tavakoli Department of Materials Engineering, Tarbiat Modares University, P.O. Box: 14115-143 Tehran, I.R. IRAN
  • Rasoul Sarraf Mamoory Department of Materials Engineering, Tarbiat Modares University, P.O. Box: 14115-143 Tehran, I.R. IRAN
چکیده مقاله:

  In this study, copper chromite (CuCr2O4) nanoparticles was prepared by inverse co-precipitation method. In this method, cupric nitrate trihydrate, (Cu (NO3)2.3H2O) and chromium nitrate nonahydrate, (Cr (NO3) 3.9H2O) with a mole ratio of 1:2 were used. Characterization of CuCr2O4 nanoparticles was performed by Fourier Transform Infrared Spectroscopy (FT-IR), Raman Spectroscopy, X-ray Diffraction Spectroscopy (XRD), Thermo-Gravimetric/Differential Scanning Calorimetry (TG-DSC), and Field Emission Scanning Electron Microscopy (FE-SEM). The results show that CuCr2O4 crystal can be obtained at temperature 520 °C. Also, phase structure of the CuCr2O4 depends on both Cu:Cr molar ratio and temperature in the starting reactants. Based on this method and under optimum conditions, the temperature for calcination (520 oC), the crystallite size of nanoparticles (18 nm), the spherical structure particles (30 to 70 nm) were obtained.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

inverse co-precipitation synthesis of copper chromite nanoparticles

in this study, copper chromite (cucr2o4) nanoparticles was prepared by inverse co-precipitation method. in this method, cupric nitrate trihydrate, (cu (no3)2.3h2o) and chromium nitrate nonahydrate, (cr (no3) 3.9h2o) with a mole ratio of 1:2 were used. characterization of cucr2o4 nanoparticles was performed by fourier transform infrared spectroscopy (ft-ir), raman spectroscopy, x-ray diffraction...

متن کامل

Synthesis and characterization of SnO2 nanoparticles by Co-Precipitation method

Tin oxide (SnO2)nanoparticles were synthesized by co-precipitation method and the synthesized nanoparticles were annealed at different temperatures for characterization. The powders were investigated with X-ray diffraction, scanning electron microscopy and optical spectroscopy. The structural characterization was carried out by X-ray diffraction which confirms the crystalline nature ...

متن کامل

Synthesis and Characterization of MnO2 Nanoparticles using Co-precipitation Technique

The thrust to develop eco-friendly procedures for the production of nanoparticles arises from the extremely recent nanotechnology research. MnO2 nanoparticles were synthesized by co-precipitation method using green chemistry. The size, structure and morphology of MnO2 nanoparticles were characterized by UV-Visible, X-Ray diffraction (XRD), FTIR techniques. The average particle size of manganese...

متن کامل

Co-precipitation Synthesis of Zinc Oxide (ZnO) Nanoparticles by Zinc Nitrate Precursor

Nanostructured zinc oxide (ZnO) materials have received considerable interest from scientists due to their remarkable performance in electronics, optics and photonics. ZnO nanoparticles were synthesized by co-precipitation method. ZnO nanoparticles were synthesized using Zn(NO3)3 and K2CO3 precursors. The structure of the obtained product was confirmed by the powder X-ray diffraction (XRD) anal...

متن کامل

Synthesis and Characterization of α-Fe2O3 Nanoparticles by Simple Co-Precipitation Method

In the past decade, magnetic nanomaterials have attracted much attention due to their physical properties and technological applications. In this work, α-Fe2O3 nanoparticles were first synthesized via a simple co-precipitation method using iron chloride hexahydrate (FeCl3.6H2O) as precursor and ammonia solution as precipitator. The samples we...

متن کامل

Co-precipitation Synthesis of Zinc Oxide (ZnO) Nanoparticles by Zinc Nitrate Precursor

Nanostructured zinc oxide (ZnO) materials have received considerable interest from scientists due to their remarkable performance in electronics, optics and photonics. ZnO nanoparticles were synthesized by co-precipitation method. ZnO nanoparticles were synthesized using Zn(NO3)3 and K2CO3 precursors. The structure of the obtained product was confirmed by the powder X-ray diffraction (XRD) anal...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 35  شماره 1

صفحات  51- 55

تاریخ انتشار 2016-02-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023