Joining of Commercial Pure Copper via Self-reacting Friction Stir Welding
نویسندگان
چکیده مقاله:
Three mm thick plates of commercial pure copper were welded via friction stir welding method using a floating bobbin tool. The effect of different process variables such as the tool transverse speed and the tool rotation speed were examined in order to create a weld with the desired properties. A defect-free weld was obtained at a rotation speed of 1400 rpm and a transverse speed of 18 mm/min with a shoulder pinching gap of 2.7 mm. After the welding process, the soundness of the welds was confirmed by non-destructive methods of visual inspection and X-ray radiography. The results of the transverse tensile test showed that the as-weld joint efficiency was 86.4%, which was higher than the joint efficiency made by the fusion welding method. The strength of the welds was such that the fracture of the workpiece was in the heat affected zone after the tensile test. On the other hand, the grain size of the weld was significantly less than the base metal. The lowest hardness around 40VHN was attributed to the middle of the thickness of the weld, while the highest hardness was in the vicinity of the lower shoulder of the tool, which was about 80 VHN.
منابع مشابه
Retracted: Optimum Rotation Speed for the Friction Stir Welding of Pure Copper
This paper [1] has been retracted as it is essentially identical in content with the published article " Elucidating of rotation speed in friction stir welding of pure copper: Thermal modeling " published in References [1] M. Jabbari and C. C. Tutum, " Optimum rotation speed for the friction stir welding of pure copper, "
متن کاملOptimization of Friction Stir Welding Tool Advance Speed via Monte-Carlo Simulation of the Friction Stir Welding Process
Recognition of the friction stir welding process is growing in the aeronautical and aero-space industries. To make the process more available to the structural fabrication industry (buildings and bridges), being able to model the process to determine the highest speed of advance possible that will not cause unwanted welding defects is desirable. A numerical solution to the transient two-dimensi...
متن کاملFriction stir welding and processing
Friction stir welding (FSW) is a relatively new solid-state joining process. This joining technique is energy efficient, environment friendly, and versatile. In particular, it can be used to join high-strength aerospace aluminum alloys and other metallic alloys that are hard to weld by conventional fusion welding. FSW is considered to be the most significant development in metal joining in a de...
متن کاملReview: friction stir welding tools
Friction stir welding (FSW) is a widely used solid state joining process for soft materials such as aluminium alloys because it avoids many of the common problems of fusion welding. Commercial feasibility of the FSW process for harder alloys such as steels and titanium alloys awaits the development of cost effective and durable tools which lead to structurally sound welds consistently. Material...
متن کاملAnalysis and Comparison of Friction Stir Welding and Laser Assisted Friction Stir Welding of Aluminum Alloy
Friction Stir Welding (FSW) is a solid-state joining process; i.e., no melting occurs. The welding process is promoted by the rotation and translation of an axis-symmetric non-consumable tool along the weld centerline. Thus, the FSW process is performed at much lower temperatures than conventional fusion welding, nevertheless it has some disadvantages. Laser Assisted Friction Stir Welding (LAFS...
متن کاملEffect of Speed and Number of Pass in Friction Stir Welding on the Mechanical and corrosion behavior of Commercial Pure Copper
The results showed that the microhardness and tensile strength of the heat-affected zone as the weakest welding zone in some samples reduced up to 30% compared to the base metal. On the other hand, a decrease in rotational speed, an increase in tool movement speed, and the number of welding passes cause grain refinement and improve mechanical properties. However, the effect of decreasing the ro...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 7 شماره 2
صفحات 44- 55
تاریخ انتشار 2020-10-30
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023