Preparation of Polyaniline-Clay Nanoadditive and Investigation on Anticorrosion Performance in Epoxy Coating

نویسندگان

  • Mahdi Ghasemi Coating Research Group, Industrial Protection Research Division, Research Institute of Petroleum Industry, N.I.O.C., Tehran, Iran
  • Mohammadreza Bagherzadeh Nanotechnology and Carbon Research Group, Faculty of Downstream Petroleum Industry, Research Institute of Petroleum Industry (RIPI), Tehran, Iran
چکیده مقاله:

The corrosion protection of mild steel by a newly developed epoxy-based coating system containing inherently conducting nanopolyaniline-clay as a nanoadditive has been studied. Polyaniline-clay anticorrosion nanoadditive (PCNA) was obtained by the direct mixing method of nanopolyaniline (0.03 wt.%) and organo-modified clay (3 wt.%) at atmospheric pressure, and XRD technique was used to study d-spacing of clay platelets in the prepared nanoadditive. PCNA was dispersed in polyaminoamide hardener matrix and was used for epoxy coating (EPCNA) preparation. The particle size of the polyaniline in hardener was determined using dynamic light scattering technique (DLS). The results revealed that the particles were in the range of 50–58 nm. The degree of exfoliation and distribution and particles size were studied by XRD and TEM in the final dried film. The corrosion protection ability of EPCNA was compared to an epoxy coating containing pure nanopolyaniline (ENPN) using electrochemical impedance spectroscopy (EIS) and salt spray methods. In addition, an investigation on the morphology of metal-coating interface by scanning electron microscopy (SEM) technique in ENPN and EPCNA samples after salt spray test showed stable oxide layer formation for ENPN and a dense stable oxide layer for EPCNA on metal surface. The results showed that the PCNA nanoadditive enhanced corrosion protection effect in comparison to pure nanopolyaniline (NPN) in the epoxy coating.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

preparation of polyaniline-clay nanoadditive and investigation on anticorrosion performance in epoxy coating

the corrosion protection of mild steel by a newly developed epoxy-based coating system containing inherently conducting nanopolyaniline-clay as a nanoadditive has been studied. polyaniline-clay anticorrosion nanoadditive (pcna) was obtained by the direct mixing method of nanopolyaniline (0.03 wt.%) and organo-modified clay (3 wt.%) at atmospheric pressure, and xrd technique was used to study d-...

متن کامل

impact of strontium aluminum polyphosphate anticorrosion pigment on performance of protective epoxy coating

the research mainly intends to evaluate performance of strontium aluminum polyphosphate as an eco friendly zinc free anticorrosion pigment in formulation of the protective primer based on epoxy resin. comparing to zinc phosphate, the most effective content of the modified pigment was determined through electrochemical impedance spectroscopy. according to pull-off, the superior sapp incorporated...

متن کامل

Cathodic electrodeposion of nano Titania along the epoxy based coating and evaluation of its anticorrosion properties

Effect of nano TiO2 particles on the corrosion properties of an epoxy based coatings was investigated. Coatings and nano Titania were applied on standard phosphated steel panels by cathodic electrodeposition simultaneously. The coated panels were immerged in 3.5 NaCl solution for 2880 hours 120 days. The SEM and EIS technique were used to investigate the electrodeposion of nano Titania particle...

متن کامل

Electrochemical evaluation of corrosion protection performance of epoxy/polyaniline-imidazole modified ZnO nanocomposite coating on mild steel

In this research, ZnO nanoparticles modified with imidazole in O-xylene solution and characterized with Fourier transform infrared FTIR spectroscopy. Then, polyaniline-ZnO unmodified and imidazole modified nanocomposites were synthesized via in-situ emulsion polymerization method. The synthesized nanocomposites were characterized by FTIR and scanning electron microscopy SEM. The anti-corrosion ...

متن کامل

effect of bataine and sulphate supplement on wool and milk characteristics and lambs performance in naine ewes

تعداد 20 رأس میش نژاد نائینی 6+-24 ماهه، با میانگین وزن 2/3-+40 کیلوگرم، همراه با 20 رأس بره های آنها در قالب طرح کاملا تصادفی اثر بتائین و مکمل سولفات بر خصوصیات شیر و پشم و عملکرد بره ها بررسی شد. میش ها بطور تصادفی در چهار تیمار قرار گرفتند. تیمارها عبارت بودند از: 1-گروه شاهد 2-بتائین (05/0 درصد ماده خشک) 3-سولفات (24/0 سولفور درصد ماده خشک 4-بتائین هرماه با سولفات. جیره غذائی طبق nrc با مح...

15 صفحه اول

Protective Performance of Polyaniline-Sulfosalicylic Acid/Epoxy Coating for 5083 Aluminum

Epoxy coatings incorporating different content of sulfosalicylic acid doped polyaniline (PANI-SSA) have been investigated for corrosion protection of 5083 aluminum alloy in 3.5% NaCl solution. The performance of the coatings is studied using a combination of electrochemical impedance spectroscopy (EIS), open circuit potential (OCP), gravimetric tests, adhesion tests, scanning electron microscop...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 5  شماره 2

صفحات  1- 11

تاریخ انتشار 2015-07-26

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023