Synthesis of Nano-Structured La0.6Sr0.4Co0.2Fe0.8O3 Perovskite by Co-Precipitation Method

نویسندگان

  • Abolghasem Ataie School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 14395-553, Tehran, Iran
  • Alireza Babaei School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 14395-553, Tehran, Iran
  • Ebrahim Mostafavi School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O. Box 14395-553, Tehran, Iran
چکیده مقاله:

Nano-structured lanthanum strontium cobalt ferrite, La0.6Sr0.4Co0.2Fe0.8O3 (LSCF), was successfully synthesized via co-precipitation method using metal nitrates as starting materials. Effects of precipitating agent and calcination temperature on the phase composition and morphology of synthesized powders were systematically studied using X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM), respectively. XRD analysis revealed that a single phase La0.6Sr0.4Co0.2Fe0.8O3 perovskite was obtained in the processed sample using ammonium carbonate as precipitating agent with a NH4+/NO3-molar ratio of 2 after calcination at 1000C for 1 h. The phase composition of products was also affected by changing pH values. Moreover, using sodium hydroxide as a precipitant resulted in a mixture of La0.6Sr0.4Co0.2Fe0.8O3 and cobalt ferrite (CoFe2O4) phases. Careless washing of the precursors can also led to the formation of mixed phase after calcination of final powders. Mean crystallite size of the obtained powders was not noticeably affected by varying calcination temperature from 900 to 1050C and remained almost the same at 10 nm, however increasing calcination temperature to 1100C resulted in sharp structural coarsening. FESEM studies demonstrate that relatively uniform particles with mean particle size of 90 nm were obtained in the sample processed with a NH4+/NO3- molar ratio of 2 after calcination at 1000C for 1 h.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

synthesis of nano-structured la0.6sr0.4co0.2fe0.8o3 perovskite by co-precipitation method

nano-structured lanthanum strontium cobalt ferrite, la0.6sr0.4co0.2fe0.8o3 (lscf), was successfully synthesized via co-precipitation method using metal nitrates as starting materials. effects of precipitating agent and calcination temperature on the phase composition and morphology of synthesized powders were systematically studied using x-ray diffraction (xrd) and field emission scanning elect...

متن کامل

Chemical Synthesis and Characterization of Perovskite NdfeO3 Nanocrystals via a Co-Precipitation Method

A facile co-precipitation method for the synthesis of well-dispersed NdFeO3 nanocrystals is developed in the presence of octanoic acid as surfactant. Co-precipitation can produce fine, high-purity, stoichiometric particles of single and multicomponent metal oxides. The product is characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microsc...

متن کامل

Surfactant Effect on the Synthesis of B4C-nano TiB Composite by Co-precipitation Method

Titanium diboride is one of the candidate materials for high temperature applications and also for control rod elements in high temperature reactors. This paper presents the experimental data on the composites of B4 C-nano TiB2 that were synthesized successfully by co-precipitation methodat 1523K. Titanium tetraisopropanol, boron carbide, isopropanol and triton x-100were used as the precursor m...

متن کامل

Synthesis and characterization of SnO2 nanoparticles by Co-Precipitation method

Tin oxide (SnO2)nanoparticles were synthesized by co-precipitation method and the synthesized nanoparticles were annealed at different temperatures for characterization. The powders were investigated with X-ray diffraction, scanning electron microscopy and optical spectroscopy. The structural characterization was carried out by X-ray diffraction which confirms the crystalline nature ...

متن کامل

SYNTHESIS OF AL2O3-NI COMPOSITE POWDERS BY CO-PRECIPITATION METHOD

The synthesis of micro-sized, uniformly distributed Al2O3-15Vol% Ni powders were studied through three step co-precipitation of hydroxides mixtures from proper solution, calcination at air atmosphere and final step of calcined powders in a carbon bed. Al and Ni hydroxide and amorphous phase were first obtained from their salt’s solutions through chemical co-precipitation method by adjusti...

متن کامل

Facile synthesis of nano-sized ZnO by direct precipitation method

In this contribution we are presenting a simple precipitation method to synthesize zinc oxide (ZnO) nanoparticles using zinc nitrate and urea in aqueous solution. The obtained precipitated compound was calcined and structurally characterized by Powder X-ray diffraction (XRD), Thermogravimetric analysis (TGA), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Fourier tr...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 48  شماره 1

صفحات  45- 52

تاریخ انتشار 2015-06-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023