M. Tavakoli Shoushtari
Materials Department, Faculty of Engineering, Shahid Chamran University, Ahvaz 61355, Iran,
[ 1 ] - Effect of ageing heat treatment on corrosion behaviorof 17-4 PH stainless steel in 3.5% NaCl
The 17-4PH alloy is a martensitic stainless steel with 3–5 wt% Cu, strengthened by the precipitation hardening. Due to excellent mechanical properties, corrosion resistance and ease of heat treatment, this alloy has unique applications in nuclear power plants and marine constructions. In this paper, the influence of ageing heat treatment, solution annealing followed by ageing at 480, 550 and 620 …
[ 2 ] - Effect of diffusion bonding temperature on microstructure properties of Zr/Ti interlayer in the diffusion bonded joints of Zr702 to A516 steel
In this study, the effect of temperature on the microstructure and reactive layer at the interface between the Ti interlayer and the base metal related to the diffusion bonding of Zr702 to A516 low alloy steel was investigated. The joining was done using the spark plasma sintering technique at temperatures of 900, 950 and 1000°C for 30 minutes. Field Emission Scanning Electron Microscope (FESEM) …
[ 3 ] - تاثیر دما بر ریزساختار و لایه واکنشی فصل‌مشترک Zr/Ti در اتصال نفوذی Zr702 به فولاد A516
در این پژوهش تاثیر دما بر ریزساختار و لایه واکنشی در فصل مشترک لایه میانی Ti و فلز پایه مربوط به اتصال نفوذی آلیاژ زیرکونیوم 702 به فولاد کم‌آلیاژ A516 بررسی شد. اتصال با استفاده از تکنیک اتصال نفوذی پلاسمای جرقه‌زن در دماهای ۹۰۰، ۹۵۰ و ۱۰۰۰ درجه سانتی‌گراد و مدت زمان ۳۰ دقیقه انجام گردید. به منظور بررسی ریزساختار فصل مشترک اتصال از میکروسکوپ نوری و الکترونی روبشی گسیل میدانی (FESEM) مجهز به آنال…