Concrete is the most widely used material for the construction of the wastewater collection, storage, and treatment infrastructure. The chemical and physical characteristics of hydrated Portland cement may make it susceptible to degradation under highly acidic conditions. As a result, some concrete wastewater infrastructure may be susceptible to a multistage degradation process known as microbi...

Corrosion of reinforcing and prestressing steel due to chloride attack is one of the major causes of deterioration of concrete structures. This is of most concern because of the associated reduction in steel cross-sectional area, spalling and loss of bond. In the case of prestressed concrete structures, the corrosion of prestressing strands can lead to a sudden failure due to higher stress leve...

Chloride induced corrosion of steel reinforcement is the main cause of deterioration of reinforced concrete marine structures. This paper investigates the relative performance of alternative repair options with respect to the deterioration of reinforced concrete bridge elements in marine environments. Focus is placed on the initiation phase of reinforcement corrosion. A laboratory study is desc...

Corrosion of steel in concrete is one of the major problems with respect to the durability of reinforced concrete structures. The majority of concrete structures perform well even after a long period of use in normal environments. However, there are various reinforced concrete structures important for our infrastructure, especially bridges and buildings, which exhibit premature damage due to en...

To study the durability of shield tunnel concrete segment under coupling multi-factors, the durability and degradation law of reinforced concrete segments under the joint action of carbonation, sulfate, chloride salt and stray current was studied by accelerated environmental and direct current (DC) power simulation test. The results show that the presence of the stray current not only accelerat...

ii DISCLAIMER The contents of this report reflect the views of the authors, who are responsible for the facts and the accuracy of the data presented herein. The contents do not necessarily reflect the official views or policies of the Virginia Department of Transportation, the Commonwealth Transportation Board, or the Federal Highway Administration. This report does not constitute a standard, s...

Acoustic emission (AE) techniques have been extensively studied and applied to nondestructive testings (NDT) of concrete and concrete structures. For damage evaluation, AE behavior of concrete under compression could be analyzed, applying the rate process theory. Based on Loland's model in damage mechanics, a relation between AE rate and the damage parameter is correlated. By quantifying intact...

A corrosion sensor for monitoring the corrosion state of cover mortar was developed. The sensor was tested in cement mortar, with and without the addition of chloride to simulate the adverse effects of chloride-contaminated environmental conditions on concrete structures. In brief, a linear polarization resistance method combined with an embeddable reference electrode was utilized to measure th...

The accuracy in the measurement of the rate of corrosion of steel in concrete depends on many factors. The high resistivity of concrete makes the polarization data erroneous due to the Ohmic drop. The other source of error is the use of an arbitrarily assumed value of the Stern-Geary constant for calculating corrosion current density. This paper presents the outcomes of a research work conducte...