A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...

corrosion of steel reinforcement is one of the most prevalent causes of reinforced concrete (rc) structures deterioration in chloride-contaminated environments. as a result, evaluating the impact of any possible corrosion-induced damages to reinforced concrete bridges strongly affects management decisions: such as inspection, maintenance and repair actions. the corrosion propagation phase is a ...

steel corrosion of bars in concrete structures is a complex process which leads to the reduction of the cross-section bars and decreasing the resistance of the concrete and steel materials. in this study, reliability analysis of a reinforced concrete beam with corrosion defects under the distributed load was investigated using the enhanced hasofer-lind and rackwitz-fiessler (ehl-rf) method base...

Corrosion of steel is one of the most important potential dangers and threats in concrete structures. Corrosion of steel embedded in reinforced concrete plays a key role in reducing the strength and durability of reinforced concrete. Several studies have proposed that alternative approaches to enhancing the performance of reinforced concrete and its resistance to corrosion. In this study, the r...

Abstract: This research examines the performance of strengthened non-uniformly corroded reinforced self-consolidating concrete (SCC) members. This paper focuses on three aspects of concrete including corrosion, concrete cover loss, and repair technique. Up to a 50% corrosion level is considered in this study. Corrosion was experimentally induced and was simulated in other cases. Twenty-six rein...

The increase in CO2 concentrations and global warming will increase the carbonation depth of concrete. Furthermore, temperature rise will increase the rate of corrosion of steel rebar after carbonation. On the other hand, compared with normal concrete, high volume fly ash (HVFA) concrete is more vulnerable to carbonation-induced corrosion. Carbonation durability design with climate change is cr...

The chloride corrosion of reinforcing steel in reinforced concrete (RC) structures is a significant reason for premature deterioration and failure of RC structures in aggressive environments such as Persian Gulf region. This is one of the most important sources of engineering and economic problems in developed countries. So, the repair and maintenance of RC structures exposed to corrosive envir...

This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each...

corrosion makes huge economic and ecologic damage all over the world. biologic corrosion of sewer pipes is considered as a serious limitation in economic perspectives. to prevent biologic corrosive damage, lining techniques can be applied by materials and aggregate resistant to attack bacterially in sewer pipes. the role of bacteria is that they convert sulfur compounds into sulfuric acid which...