Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-is...

BACKGROUND Slow crack growth can be described in a v (crack velocity) versus KI (stress intensity factor) diagram. Slow crack growth in ceramics is attributed to corrosion assisted stress at the crack tip or at any pre-existing defect in the ceramic. The combined effect of high stresses at the crack tip and the presence of water or body fluid molecules (reducing surface energy at the crack tip)...

fast fracture is one of the major failure modes in brittle polymers. generally, crack growth in these polymers may occur under combined tensile-shear loading. however, the fracture test data reported previously for some dental restorative resins can not be predicted by using the available fracture criteria.in this paper, a modified fracture criterion is used for estimating the fracture load for...

In situ ultrasonic fatigue with a cyclic frequency of 20 kHz was employed in an environmental scanning electron microscope (ESEM) to characterize fatigue crack formation and growth in the near alpha titanium alloy Ti–6242S. The role of environment on small fatigue crack initiation and growth was investigated in vacuum and in variable pressures of saturated water vapor, as well as in laboratory ...

Fatigue cracking is one of the most common failure modes of various load-bearing structures. Even though sensors of many different types have been developed for crack detection, very few can monitor crack growth with a high sensitivity. This paper presents an antenna sensor that is capable of monitoring the growth of fatigue cracks with a sub-millimeter resolution. According to microstrip patch...

Title: Crack Growth During Brittle Fracture in Compression. Author: Bartlett W. Paulding, Jr. Submitted to the Department of Geology and Geophysics February 9, 1965 in partial fulfillment of the requirements for the degree of Doctor of Philosophy at the Massachusetts Institute of Technology. Photoelastic analysis of several two-crack arrays predicts that compressive fracture is initiated at cra...

The mechanisms of fatigue-crack propagation in ceramics and intermetallics are examined through a comparison of cyclic crack-growth behavior in ductile and brittle materials. Crack growth is considered to be a mutual competition between intrinsic mechanisms of crack advance ahead of the crack tip, which promote crack growth, and extrinsic mechanisms of crack-tip shielding behind the tip, which ...

OBJECTIVES The objective of this in vitro study was to evaluate the fatigue crack growth properties of the dentin/resin adhesive interface. METHODS Compact tension (CT) specimens were prepared from coronal dentin, resin composite, and dentin bonded to resin composite using Optibond Solo Plus adhesive. All specimens were then subjected to cyclic Mode I loading while fully hydrated at a stress ...

in this paper, the mechanical behavior of three-phase inhomogeneous materials is modeled using the meso-scale model with lattice beams for static and dynamic analyses. the timoshenko beam theory is applied instead of the classical euler-bernoulli beam theory and the mechanical properties of lattice beam connection are derived based on the continuum medium using the non-local continuum theory. t...