The evolution of surface damage in bilayers due to cyclic spherical indentation in the presence of incompressible lubricant is studied using an all-transparent glass/polycarbonate system as amodel formore practical applications such as dental crowns and rolling contact fatigue. In situ observations and post-mortem material sectioning reveal that inner cone cracks evolve sequentially from the co...

The natural initiation and growth of short cracks in Inconel 718 U-notch specimens has been studied at 600C in air. U notches were introduced through broaching, and hardness traces and optical microscopy on cross sections through the U notch broaching showed that the broaching process had introduced a deformed, work hardened layer. Fatigue tests were conducted under load control using a 1-1-1-1...

A first intermediate roll of Sendzirmir mills was failure by surface spalling during operation. After analyzing by visual, stereo microscope, optical microscope, scanning electron microscope, glow-discharged spectrometer and hardness test, respectively, the results show that some voids and cracks existed on the contact surface as well as subsurface. Further examination verified inadequate hardn...

Electro Discharge Machining (EDM) is a very efficient machining process widely used in manufacturing components of complicated geometry. Based on its nature, i.e. material removal by electric discharge, the process induces thermal stresses that in turn result in generation of wide spread micro-cracks on the surface of the machined part. In this paper the influence of EDM characteristic paramete...

Cracks, the important factor of structure failure, reflect structural damage directly. Thus, it is significant to realize distributed, real-time crack monitoring. To overcome the shortages of traditional crack detectors, such as the inconvenience of installation, vulnerability, and low measurement range, etc., an improved topology-based cable sensor with a shallow helical groove on the outside ...