This paper presents low cycle fatigue (LCF) life prediction of a coated and uncoated exhaust manifolds. First Solidworks software was used to model the exhaust manifolds. A thermal barrier coating system was applied on the tubes c of the exhaust manifolds, consists of two-layer systems: a ceramic top coat (TC), made of yttria stabilized zirconia (YSZ), ZrO2-8%Y2O3 and also a metallic bond coat ...

The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...

In this paper, the lap splice length and the long-term (fatigue) performance of lap-spliced carbon FRP laminates were investigated. Lap-spliced CFRP coupon specimens were fabricated with a splice length of 12.7, 25.4, 38.1, 50.8, 76.2, and 101.6 mm. To eliminate the bending on the lap splice joint, a symmetric specimen configuration was adopted. The width of the specimens was 38.1 mm. These spe...

OBJECTIVES To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide (Al2O3) particles at different pressures. MATERIALS AND METHODS Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abra...

A study has been made of high-cycle fatigue in 2-μm thick structural films of ntype, polycrystalline silicon for MEMS applications. Using an “on-chip” test structure resonating at ~40 kHz, such thin-film polysilicon is shown to display “metal-like” stress-life fatigue behavior in room air environments, with failures occurring after lives in excess of 10 cycles at stresses as low as half the fra...

Metallic shear panel dampers (SPDs) have been widely adopted in seismic engineering. In this study, axial and torsional specimens of four types of metallic damping materials, including three conventional metallic steels as well as low yield strength steel 160 (LYS160), were tested in order to investigate the material response under repeated large plastic strain and low cycle fatigue between 10 ...

Fatigue is the primary cause of failure of crankshafts in internal combustion engines. The cyclic loading conditions and the stress concentrations in the crank pin fillets are unavoidable, and can result in fatigue failure. The objectives of this study were to compare the fatigue behavior of forged steel and ductile iron crankshafts from a one-cylinder engine as well as to determine if the fati...

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batc...