Solid-state nanopore has captured the attention of many researchers due to its characteristic of nanoscale. Now, different fabrication methods have been reported, which can be summarized into two broad categories: "top-down" etching technology and "bottom-up" shrinkage technology. Ion track etching method, mask etching method chemical solution etching method, and high-energy particle etching an...

The synchrotron radiation (SR) stimulated etching of silicon elastomer polydimethylsiloxane (PDMS) using XeF(2) as an etching gas has been demonstrated. An etching system with differential pumps and two parabolic focusing mirrors was constructed to perform the etching. The PDMS was found to be effectively etched by the SR irradiation under the XeF(2) gas flow, and the etching process was area-s...

High speed directional etching of non conventional materials like Quartz, Lithium Niobate and Lead Titanate is still insufficiently developed for producing high aspect ratio microstructures. Compared to deep silicon etching, the plasma etching of these materials has suffered from limitations in achievable depth, aspect ratio, verticality and smoothness of surfaces. Deep etching with nearly vert...

The realization of flat surfaces on the angstrom scale is required in advanced devices to avoid loss due to carrier (electron and/or photon) scattering. In this work, we have developed a new surface flattening method that involves near-field etching, where optical near-fields (ONFs) act to dissociate the molecules. ONFs selectively generated at the apex of protrusions on the surface selectively...

Dry etching is one of the elemental technologies for the fabrication of optical devices. In order to obtain the desired shape using the dry etching process, it is necessary to understand the reactivity of the materials being used to plasma. In particular, III-V compound semiconductors have a multi-layered structure comprising a plurality of elements and thus it is important to first have a full...

The optimization of etchant parameters in wet etching plays an important role in the fabrication of semiconductor devices. Wet etching of tetramethylammonium hydroxide (TMAH)/isopropyl alcohol (IPA) on silicon nanowires fabricated by AFM lithography is studied herein. TMAH (25 wt %) with different IPA concentrations (0, 10, 20, and 30 vol %) and etching time durations (30, 40, and 50 s) were in...

Figure 1 . Anisotropic etching of graphite by H 2 -plasma. a–c) AFM images of pristine, 50 W plasma-etched, and 100 W plasma-etched graphite. Plasma etching was performed at 500 ° C for 2 h. Magnifi ed images for the marked areas are shown. d) Measured maximum etching rate of graphite at various etching temperatures. The plasma power was 100 W. Solid lines represent Lorentzian line shape fi ts....