Sphere-like shaped cobalt oxide nanoparticles (Co3O4) were synthesized by a simple wet chemical method using cobalt chloride as precursor and cetyl trimethylammonium bromide (CTAB) as surfactant. Their structural and surface morphologial properties were characterized by high resolution transmission electron microscopy (HRTEM), field emission scanning electron microscopy (FESEM) and X-ray diffra...

We present here comparative assessments of murine lung toxicity (biocompatibility) after in vitro and in vivo exposures to carbon (C-SiO2-etched), carbon-silica (C-SiO2), carbon-cobalt-silica (C-Co-SiO2), and carbon-cobalt oxide-silica (C-Co3O4-SiO2) nanoparticles. These nanoparticles have potential applications in clinical medicine and bioimaging, and thus their possible adverse events require...

Sphere-like shaped cobalt oxide nanoparticles (Co3O4) were synthesized by a simple wet chemical method using cobalt chloride as precursor and cetyl trimethylammonium bromide (CTAB) as surfactant. Their structural and surface morphologial properties were characterized by high resolution transmission electron microscopy (HRTEM), field emission scanning electron microscopy (FESEM) and X-ray diffra...

catalysts with the formula of laco(1+x)o(3+δ), where 0 ≤ x ≤ 1, were studied for oxidation of co and c2h6 in a synthetic exhaust gas, comprising 6.0 % co and 0.2 % c2h6 in ar. ethane was selected as a model for hydrocarbons in the exhaust gas. the performance of catalysts is correlated to their properties, particularly their redox in oxidizing and reducing atmospheres. xrd patterns show perovsk...

Double-shell cobalt monoxide (CoO) hollow particles were successfully synthesized by a facile and effective one-pot solution-based synthetic route. The inner architecture and outer structure of the double-shell CoO hollow particles could be readily created through controlling experimental parameters. A possible formation mechanism was proposed based on the experimental results. The current synt...

Cobalt oxide (Co3O4) was homogeneously coated on multiwalled carbon nanotube through a simple chemical deposition method and employed in supercapacitor electrodes. SEM image indicated the uniform distribution of Co3O4 nanoparticles on the surface of the multiwalled carbon nanotube. A maximum specific capacitance of 273 Fg(-1) was obtained at the charge-discharge current density of 0.5 Ag(-1). A...

Effects of Fe2O3 addition (2-20 wt%) with 1 h mechanical activation on redox reactions of Co3O4 were studied by TG/DSC, SEM, and XRD analyses. The results showed that a Fe2O3 addition from 2 to 15 wt% increases the oxygen release from 1.4 to 3.4 wt% and decreases the reduction onset temperature from 1030 to 960 °C, while it increases the oxygen uptake value and re-oxidation onset temperature re...

in this paper, macrocyclic cobalt(ii) complexes [col1](no3)2.4h2o (1) and [col2](no3)2.2h2o (2) have been synthesized from the reaction of dialdehydes 1,2-bis(2-formylphenyl)ethane and 1,3-bis(2-formylphenyl)propane, co(no3)2.6h2o and 1,2-cyclohexanediamine with molar ration 1:1:1 in methanole and characterized by elemental analyses and ft-ir spectroscopy. then used as precursors for preparatio...

In this report, functional one-dimensional (1-D) Pt-Co3O4 heterostructures with enhanced electrochemical properties were synthesized via colloidal polymerization of polymer-coated ferromagnetic cobalt nanoparticles (PS-CoNPs). Colloidal polymerization of dipolar nanoparticles into hollow metal-semiconductor nanowires was achieved via a consecutive galvanic replacement reaction between Co and Pt...

A low-concentration cobalt (∼6 at%) and manganese (∼3 at%) bimetallic oxide catalyst supported on ceria nanorods (CoMnOx/CeO2), as well as its related single metal oxide counterparts (CoOx/CeO2 and MnOx/CeO2) was synthesized via a deposition-precipitation approach. The fresh samples after air-calcination at 400 °C were tested under the reaction conditions of CO oxidation, and showed the followi...