Residual compressive stress can improve fretting fatigue strength. In this paper, the effects of residual stress on fretting fatigue of Al 2024-T351 alloy specimens are studied using a numerical approach. The extended finite element method combined with the cyclic cohesive zone model is adopted to model fretting fatigue crack growth behavior. It is shown that residual stress changes the frettin...

The fracture and crack growth of mechanical structures is a usual phenomenon which is due to the application of tensile, cyclic loading or thermal stresses on the structure. So introducing of methods to prevent the crack growth is useful. Afterward, one of the repairing methods of crack growth, consisting to make a hole in the crack tip to elimi-nate the sharp corners, was explained. This metho...

The solution of three-dimensional cracks (arbitrary surfaces of discontinuity) in solids and structures is considered. The BEM, developed based on the symmetric Galerkin BIEs, is used for obtaining the fracture solutions at the arbitrary crack-front. The finite element method is used to model the uncracked global (built-up) structure for obtaining the stresses in an otherwise uncracked body. Th...

Abstract: To ensure the rail transportations safety, evaluation of fatigue behavior of the rail steel is necessary. High cycle fatigue behaviour of a rail steel was the subject of investigation in this research using fracture mechanics. Finite element method (FEM) was used for analyzing the distribution of the stresses on the rail, exerted by the external load. FEM analysis showed that the ...

In this paper, the effect of interference fit on fatigue life of holed plate of mechanical joints was investigated experimentally. Fatigue tests were carried out on the holed specimens of Al-alloy 7075-T6 alloy. The interference fit process consists of force fitting a fastener into the hole with a negative clearance (diameter of the fastener is larger than of the hole) that produces beneficial ...

The influence of tubule orientation on the transition from fatigue to fatigue crack growth in human dentin was examined. Compact tension (CT) and rectangular beam specimens were prepared from the coronal dentin of molars with three unique tubule orientations (i.e., 0 degrees , 45 degrees and 90 degrees). The CT specimens (N=25) were used to characterize fatigue crack initiation and steady-state...

The mean and the life-limiting behavior under fatigue of the nickel-based superalloy, IN100, separated (or converged) as a function of stress level and dwell loading. This behavior was related to the control of the life-limiting behavior by the smallcrack growth regime, producing its much slower response to stress level and dwell-time, relative to the mean-lifetime behavior. The lifetime probab...

In this study, the crack growth behavior in a filled elastomer, containing hard particles embedded in a rubbery matrix, was investigated. The specimen was tested at a constant strain rate of 0.067 cm/cm/min at room temperature. Two initial crack lengths, 2.54 mm and 12.7 mm, were considered. A hybrid experimental-numerical method was used to calculate the Jintegral value. They also revealed tha...

The addition of liquid-filled urea-formaldehyde (UF) microcapsules to an epoxy matrix leads to significant reduction in fatigue crack growth rate and corresponding increase in fatigue life. Mode-I fatigue crack propagation is measured using a tapered doublecantilever beam (TDCB) specimen for a range of microcapsule concentrations and sizes: 0, 5, 10, and 20% by weight and 50, 180, and 460 lm di...

This paper presents a low cycle fatigue life curve by simulating a crack in a cover plate welded moment connection. Initiation of ductile fracture in steel is controlled by growth and coalescence of micro-voids. This research used a numerical method using finite element modeling and simulation of ductile crack initiation by a micromechanical model. Therefore, a finite element model of a cover p...