Mechanical behavior of two-layer metal laminate structures under low-speed impact loading was investigated experimentally and numerically. The experimental results were just used for validation of numerical results. Then numerical modeling was used to study the behavior of metal laminates in details. The mechanical behavior of the metal laminate structures under impact loading was found to be d...

The present work study flexural and tensile behavior of short Kenaf fiber reinforced composites. The fibers are chemically treated in 2% NaOH solution at room temperature. Short fibers of 4mm and 8 mm are used in the present work. The composite lamina is prepared by hand molding using isopthalic polyester resin. Flexural test and tension tests are carried out as per ASTM standards. The flexural...

The production of large and complex parts using fiber composite materials is costly due to the frequent formation of voids, porosity and waste products. By embedding different types of sensors and monitoring the process in real time, the amount of wastage can be significantly reduced. This work focuses on developing a knowledge-based method to improve and ensure complete impregnation of the fib...

The rise in cutting temperatures during the machining process can influence the final quality of the machined part. The impact of cutting temperatures is more critical when machining composite-metal stacks and fiber metal laminates due to the stacking nature of those hybrids which subjects the composite to heat from direct contact with metallic part of the stack and the evacuated hot chips. In ...

Composite materials such as fiber metal laminates combine the advantages of metallic and fiber-reinforced polymers. Hence, these are great interest for thin-walled structures in lightweight engineering. Due to structure materials, damage laminate components occur more frequently inside than with conventional materials. Since detection interlaminar is complicated compared external damage, it one...

Exposing a laminate structure to thermal cycles and to temperatures close to the curing temperature, followed by mechanical fatigue, cause interlaminar and intralaminar cracks leading to degradation of the mechanical properties. The effect of thermal and mechanical fatigue, as well as thermal aging, on carbon fiber composite laminate structures is under study in the present paper.

The present study reports the influence of fiber orientation, laminate sequence and fabric type on the inherent nonlinearity of intact carbon fiber/epoxy composites using nonlinear resonant ultrasonic spectroscopy (NRUS) [1-2]. Fiber orientation of the CFRP samples were changed relative to the length of the sample. Since the fundamental flexural mode is excited, the properties of the composite ...

The work aimed to assess the failure progress in a glass fiber-reinforced polymer laminate with a 3D-woven and (as a comparison) plain-woven reinforcement, during static bending, using acoustic emission signals. The innovative method of the separation of the signal coming from the fiber fracture and the one coming from the matrix fracture with the use of the acoustic event's energy as a criteri...