influences of temperature as well as holding time on physical and mechanical properties of fir wood were studied in this work during the oleothermal wood modification. wood samples were cut and treated oleothermally in the soybean oil at 200 and 230°c for the holding time of 1, 3 and 5 hours. weights and the dimensions were measured before and after treatment. bending strengths, water absorptio...

partial replacement of formaldehyde with furfural in the urea-formaldehyde resin on the formaldehydeemission, physical and mechanical properties of particleboard was investigated. the modulus ofrupture (mor), modulus of elasticity (moe), internal bond (ib), water absorption (wa), thicknessswelling (ts) and formaldehyde emission (fe) of poplar particleboards made with the modifiedresins were mea...

Specular X-ray reflectivity (XR) and quartz crystal microbalance (QCM) measurements were used to determine the absorption of water into thin poly(4-ammonium styrenesulfonic acid) films from saturated vapor at 25 degrees C. The effect of film thickness on the absorption kinetics and overall absorption was investigated in the range of thickness from (3 to 200) nm. The equilibrium swelling of all ...

To investigate the possibility of using bamboo-bundle laminated veneer lumber (BLVL) as a cooling tower packing material, the water absorption rates, thickness swelling rates, and flexural properties of three different composite materials were studied. The BLVL was combined with either 12% or 24% phenol formaldehyde resin (PF), and the moso bamboo strips were exposed to water baths at three dif...

Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...

Fire-retarding properties of wollastonite nanofibers in poplar wood (Populus nigra) were studied here. Some physical properties such as water absorption, volumetric swelling and anti-swelling efficiency (ASE) were also measured. Specimens were prepared according to the ISO 11925 specifications for the fire-retarding properties and according to the ASTM D4446 -2002 specifications for th...

Untreated and nano-based compound treated chestnut, wild cherry, fir, and black pine wood samples were immersed in water at four different temperature levels. It was found that the nano-based compound was a very effective agent for lowering both the initial and maximum equilibrium transverse swelling of wood. However, the latter were found to have similar trends as the initial swelling properti...

Effects of drying temperature and artificial UV irradiation on the pH of veneer surfaces, water absorption, thickness swelling, as well as shear strength of plywood manufactured from untreated and treated veneer sheets were evaluated. Rotary cut veneer sheets from beech (Fagus orientalis Lipsky) log were selected. The veneer sheets were dried at either 100C or 180C after peeling. Then the sur...