For rehabilitation of damaged concrete structures, the durability of repair overlay is a very important issue. Self-compacting concretes (SCC) are known as a suitable repair overlay materials. In this study, the durability of different self-compacting lightweight aggregate concretes (LWSCC) and effect of lightweight aggregate type on them is investigated. 3 mix designs of LWSCC containing three...

Under badly environmental conditions as well as complex loads, corrosion of embedded reinforcing steel bars in concrete is common for reinforced concrete (RC) structures. Fatigue of corrosion reinforcing steel bars is a key problem for old RC bridges. To assess the residual fatigue life of aged existing RC bridges, the most new study information on fatigue of natural corrosion reinforcement is ...

Corrosion is one of the major problems affecting the durability of reinforced concrete (RC) structures. This paper investigates the effect of rebar corrosion on the performance of reinforced self-consolidating concrete (SCC) members and the effectiveness of repair. A control RC member, which has no corrosion problem, was prepared to compare against corroded and repaired members. A number of rei...

The life of a concrete bridge exposed to deicing salt or seawater has often been limited by corrosion of the steel reinforcement. The service life of a concrete structure, degraded by corrosion, is considered to be the sum of the initiation and propagation periods. The initiation phase is the time required for sufficient accumulation of aggressive species at the rebar surface to initiate corros...

A Gaussian function is proposed to describe the non-uniform spatial distribution of corrosion products as measured from chloride-exposed reinforced concrete specimens using backscattered electron imaging and image analysis. The model provides a good fit to the observed data and limited data sets reported in the literature. Subsequently it is used as an input into a finite element analysis to pr...

This study presents and implements a corrosion-monitoring wireless sensor platform, EPS (Events as Power Source), which monitors the corrosion events in reinforced concrete (RC) structures, while being powered by the micro-energy released from the corrosion process. In EPS, the proposed corrosion-sensing device serves both as the signal source for identifying corrosion and as the power source f...

Microbiologically induced deterioration (MID) causes corrosion of concrete by producing acids (including organic and inorganic acids) that degrade concrete components and thus compromise the integrity of sewer pipelines and other structures, creating significant problems worldwide. Understanding of the fundamental corrosion process and the causal agents will help us develop an appropriate strat...

This paper presents an experimental investigation on the crack width induced by the corrosion of reinforcing steel bars in concrete. Reinforcing steel bars with different diameters were corroded using an accelerated test in three types of concrete members, including 24 beams with corroded stirrup and 20 beams with corroded longitudinal reinforcing steel bars. The corrosion patterns and rusts ch...

Corrosion of the steel reinforcement in concrete requires manual and costly repair procedures to prevent premature failure of constructions. Although preventive measures during the construction phase are often implemented but early corrosion may still occur. The primary reason for premature corrosion is crack formation in the concrete cover. Larger cracks as well as a network of finer cracks al...