Fracture assessment of U- and V-notches is important in mechanical engineering. One can use the J-integral as fracture parameter in order to predict the critical fracture load in notches. The critical value of the J-integral in cracks is a function of the material properties. In notches, however, the material properties as well as the notch dimensions affect this critical value (named fracture ...

Crack propagation modeling in quasi-brittle materials such as concrete is essential for improving the reliability and load-bearing capacity assessment. Crack propagation explains many failure characteristics of concrete structures using the fracture mechanics approach. This approach could better explain the softening behavior of concrete structures. A great effort has been made in developing nu...

OBJECTIVE We evaluated the detachment force, amount of deformation, fracture mode, and pull-out force of 3 different wires used for bonded lingual retainer fabrication. METHODS We tested 0.0215-inch five-stranded wire (PentaOne, Masel; group I), 0.016 × 0.022-inch dead-soft eight-braided wire (Bond-A-Braid, Reliance; group II), and 0.0195-inch dead-soft coaxial wire (Respond, Ormco; group III...

In this work, fracture behavior of multilayered unidirectional graphite/epoxy composite (T800/3900-2) materials is investigated. Rectangular coupons with a single-edged notch are studied under geometrically symmetric loading configurations and impact loading conditions. The notch orientation parallel to or at an angle to the fiber orientation is considered to produce mode-I or mixed-mode (mode-...

Cracked and un-cracked Brazilian disc specimens subjected to diametral compression were used for conducting fracture toughness and tensile strength experiments on a polymer concrete (PC) material. The value of mode I fracture toughness (KIc) was determined from the center- cracked Brazilian disc and the indirect tensile strength (σt) was obtained from the un-cracked Brazilian disc specimen. The...

A nonlinear elastic foundation model has been developed to predict the mixed-mode (modes I and II) delamination failure of laminated composites. Two types of nonlinear elastic foundations were used to represent pure mode I and pure mode II components of the material failure ahead of the crack tip. One is a tension spring foundation for mode I component and the other is a shear spring foundation...