Reduced-activation ferritic/martensitic steels have been developed by replacing molybdenum by tungsten and niobium by tantalum in commercial elevated-temperature Cr–Mo steels to reduce half-life of radioactive isotopes. The objective of this study was to investigate tensile properties of a reduced-activation ferritic/martensitic steel (9Cr-2WVTa) in normalized-tempered (NT) and quenched-tempere...

An effect of rolling temperature on the mechanical properties and microstructural evolution of an Al-Mg-Si alloy was studied. The material was rolled up to a true strain of ∼0.7 at three different temperatures viz; room temperature, liquid propanol and liquid nitrogen. The liquid nitrogen rolled sample exhibited superior properties with a yield and tensile strength of 332 MPa and 364 MPa, respe...

Abstract: A pulse-echo technique, based on ultrasonic "long-bar" mode (LBM) velocity measurements, working up to 1700°C is described. Magnetostrictive transducers and ultrasonic lines used in a 40-85 kHz frequency range are detailed. The conditions of choice of fundamental parameters (frequency, line geometry, sample size) are discussed in relation with the nature and the microstructure of ...

This study examines the effect of tensile test temperatures ranging from 50°C to 600°C on the tensile properties of a modified 9Cr-1Mo ferritic steel (T91) and a 316L stainless steel (SS) after high energy proton irradiation at about 35°C-67°C. After 1-3 dpa, the proton-irradiated T91 steel was tensile tested at temperatures from 50°C to 600°C. It was observed that the yield strength and ultima...

The samples were prepared according to the routine work for sample preparation in dental laboratories. After reaching dough stage, the mixture packed into dumbbell shaped of stainless steel mould and pressed in a hydraulic bench press for 25 min at room temperature. For heat-cure, the polymerization cycle was carried out using water bath, while self-cure done at room temperature. The residual m...

This work presents the effect of various wear environments like 20% soil & 80% sand and 40% soil & 60% sand on as received and carburized mild steel sample at different load like 75N, 200N & 375N and at different tempering temperature like 200oC, 250oC & 300oC. The mild steel sample was carburized at 950oC. The heat treatment after carburization has been acknowledge that at some instant it impr...

In the present study, a better knowledge of the influence of plasticizer content, storage relative humidity and film thickness on the mechanical properties of high amylose corn starch based films gelatinized at low temperature, is presented. The mechanical properties, tensile strength and percentage of elongation at break of high amylose corn starch films plasticized with glycerol were evaluate...