Blown-powder laser surface alloying was performed on the magnesium alloy AZ91D with Al-Si alloy powder to improve corrosion resistance. Characterization by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and x-ray diffraction (XRD) analysis revealed that intermetallic compounds (IMCs) of Mg2Si, Al12Mg17 and Al3Mg2 were formed in the matrix of α-Mg and Al solid solutions...

The microstructure and residual stresses of an AA6040 Al to AZ31B Mg friction stir weld are studied using scanning electron microscopy and X-ray diffraction. The complex material flow promoted by the friction stir welding process results in a fine grained structure in the stir zone of both materials due to dynamic/recovery recrystallization. The interface between the materials is characterized ...

In the present study, friction spot welding or refill friction stir spot welding was performed to consolidate dissimilar AA5754 Al and AZ31 Mg alloys. The intermetallic compounds of Al12Mg17 and Al3Mg2 were primarily found in the weld, distributed at the interface between the base materials and in the Al top sheet. The distribution of the intermetallic compounds and the interfacial area between...

in this work, a new aluminum matrix nanocomposite reinforced with beta-magnesium aluminide nanoparticles was produced by powder metallurgy technique. the prealloyed al-40 wt.% mg intermetallic ingot was milled for 100 hours to synthesize β-al3mg2 nanoparticles with the average size of 25 nm. different amounts of nanoparticles were added to al matrix powder and the mixture was then milled for 10...

In this study, HEA/Al composite interlayer was used to fabricate Ti/Mg bimetal composites by solid-liquid compound casting process. The Al layer prepared on the surface of TC4 alloy hot dipping, and FeCoNiCr HEA magnetron sputtering onto layer. influence thickness pouring temperature interface evolution investigated based SEM observation thermodynamic analysis. Results indicate that sluggish di...

The valence states of Mg-Al alloys are compared to those of reference materials (pure Mg and Al metals, and intermetallics). Two methods based on X-ray emission spectroscopy are proposed to determine the phases and their proportion: first, by analyzing the Al valence spectra of the Mg-rich alloys and the Mg valence spectra of the Al-rich alloys; second, by fitting with a linear combination of t...

Disks of commercial Al-1050 and ZK60A alloys were stacked together and then processed by conventional high-pressure torsion (HPT) through 1 and 5 turns at room temperature to investigate the synthesis of an Al–Mg alloy system. Measurements of microhardness and observations of the microstructures and local compositions after processing through 5 turns revealed the formation of an ultrafine multi...