modelling of crack propagation by finite element method under mixed mode conditions is of prime importance in fracture mechanics. this paper describes an application of finite element method to the analysis of mixed mode crack growth in linear elastic fracture mechanics. crack growth process is simulated by an incremental crack-extension analysis based on the maximum principal stress criterion,...

Modeling of crack propagation by a finite element method under mixed mode conditions is of prime importance in the fracture mechanics. This article describes an application of finite element method to the analysis of mixed mode crack growth in linear elastic fracture mechanics. Crack - growth process is simulated by an incremental crack-extension analysis based on the maximum principal stress c...

Lithium-ion batteries have become a widely-used commodity for satisfying the world’s mobile power needs. However, the mechanical degradation of lithium-ion batteries initiated by micro cracks is considered to be a bottleneck for advancing the current technology. This study utilizes a finite element method-based virtual crack closure technique to obtain particleand crack-sizedependent estimates ...

The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...

The propagation of cracks in graded materials under monotonic and cyclic loading was investigated via experiment and simulation. Graded alumina/epoxy composite specimens exhibiting a variation in composition from 5% to 65% epoxy, representing a twenty-fold variation in Young’s modulus, across a region of width between 6 and 20 mm, were produced by a multistep infiltration technique. Crack initi...

Successful arrest and retardation of fatigue cracks is achieved with an in situ self-healing epoxy matrix composite that incorporates microencapsulated dicyclopentadiene (DCPD) healing agent and Grubbs first generation Ru catalyst. Healing agent is released into the crack plane by the propagating crack, where it polymerizes to form a polymer wedge, generating a crack tip shielding mechanism. Du...

In this paper, the fatigue and fracture properties of bovine dentin are evaluated using in vitro experimental analyses. Double cantilever beam (DCB) specimens were prepared from bovine maxillary molars and subjected to zeroto-tension cyclic loads. The fatigue crack growth rate was evaluated as a function of the dentin tubule orientation using the Paris law. Wedge-loaded DCB specimens were also ...

The role of grain bridging in affecting the initial rising portion of the R-curve and the transient, non-steady-state behavior of short cracks during (cyclic) fatigue-crack propagation has been quantitatively examined in a 99.5% pure alumina. Fatigue-crack growth properties for both long and short ( af < 2 mm) cracks emanating from machined notches (root radius, 15–150 m) were investigated, whe...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...

We recently developed a method to measure cortical bone fracture initiation toughness using a double-notched beam in four-point bending. This method was used to test the hypothesis that mineralization around the two notch roots is correlated with fracture toughness and crack extension (physical damage). Total energy absorbed to failure negatively correlated with average mineralization of the be...