Wear phenomena understanding of implants is a challenge: friction-corrosion of biomaterials, which constitute orthopaedic implants, is a significant issue concerning the aseptic loosening. This work aims at studying AISI 316L/bone cement friction which is a tribological problem related to hip joint cemented prostheses. This study focuses on the ionic strength effect on the tribological behaviou...

For periods up to 21 days human bone marrow was cultured in control conditions that favor the proliferation and differentiation of osteoblastic cells. The effect of AISI 316L corrosion products and the corresponding major separate metal ions (Fe, Cr, and Ni) were studied in three different phases of the culture period in order to investigate the effects of metal ions in cell populations represe...

Complex two-component peak of anelastic mechanical losses was observed in multicomponent substitutional austenitic alloys after prior plastic deformation. In AISI 316L, AISI 316LN, AISI 310 and AISI 304 austenitic stainless steels, this peak is situated in the wide range of temperature from 200 to 400K. Characteristics of the observed peak for different thermo-mechanical treatments were studied...

The study comprises evaluation of suitability of passive layer created on the surface of AISI 316L stainless steel for products that are intended to have contact with blood. For that purpose, prior to and after chemical passivation, samples were subject to 7 day exposure in artificial plasma at the temperature of T=37°C. Next, tests of metallic ions infiltration from the surface to the solution...

The effect of several Almen intensities of shot peening on the corrosion behavior, surface roughness, micro hardness profiles, and residual stresses of stainless steel AISI 316 L were investigated. Hydroxyapatite coating (HA) were applied to shot peened materials to improve their corrosion resistance. The corrosion behaviour were studied using potentiodynamic polarization. The electrochemical t...

In this study, the synergistic effects of abrasion and corrosion on AISI 316L stainless steel have been investigated using a micro-abrasion test rig. A series of results from abrasioncorrosion tests conducted using the micro-abrasion rig are presented. AISI 316L stainless steel has been studied under both pure abrasion and abrasion-corrosion conditions simulated by either distilled water or 3.5...

A simple and effective method without vacuum to control the wetting properties of AISI 316L stainless steel using femtosecond laser pulses at high repetition rate has been developed. Both hydrophilic and hydrophobic surfaces were formed by creating micro-conical structures on the surface with femtosecond laser irradiation in air. The scan speed was found to be an effective parameter in controll...

In this study, electrochemical behaviour of passive films formed on AISI 316L stainless steel (AISI 316L) in three acidic solutions concentrations (0.3, 0.6, and 0.9M HNO3) under open circuit potential conditions were evaluated by potentiodynamic polarization, Mott–Schottky analysis and electrochemical impedance spectroscopy (EIS) techniques. The potentiodynamic polarization results showed that...

behaviors of stress corrosion cracking (scc)in martensitic stainless steel(aisi 420) and low carbon austenitic stainless steel (aisi 316l) have been compared under different conditions of temperature, environment (mgcl2), and strain rate. the results show that decreasing strain rate has detrimental effect on mechanical properties of both steels, including their strength and ductility. fractogra...

This article presents corrosion data and microstructural analysis data of austenitic stainless steels AISI 316L and AISI 347H exposed to supercritical water (25 MPa, 550 °C) with 2000 ppb of dissolved oxygen. The corrosion tests lasted a total of 1200 h but were interrupted at 600 h to allow measurements to be made. The microstructural data have been collected in the grain interior and at grain...