Corrosion-resistant coatings based on the iron aluminide intermetallic compound Fe3Al are currently being investigated for fossil energy applications. Fe3Al possesses excellent intrinsic high-temperature oxidation and sulfidation resistance, and a significant effort has been made in the development of bulk alloys based on it. While substantial progress has been made, the widespread use of these...

the synthesis of nanocrystalline fe3al powder by mechanical alloying as well as the structural ordering of the synthesized fe3al particles during the subsequent thermal analysis were investigated. mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. the synthesized powders were cha...

the use of fe-al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. the coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚c in an argon controlled atmosphere. the optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. the microstructure ...

The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour.&#10The microstructu...

The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. The microstructure...

In the present investigation, dissimilar friction welding between AA6063-T6 and SS 304L materials of pipe joint configuration with an outer diameter 88.90 mm a wall thickness 5.4 was performed. Four different experimental conditions were varied based on visual inspection after each weld. The welded joints evaluated by vacuum leak detection, thermal shock test, pneumatic pressure tensile optical...

Fe3Al intermetallics (Fe3Al, Fe3Al-Zr, Fe3Al-Zr,Mo and Fe3Al-Zr,Mo,Nb) were oxidized at 950 C in dry and humid (11 vol% water) synthetic air. Thermogravimetric measurements showed that the oxidation rates of the tested intermetallics were lower in humid air than in dry air (especially for Fe3Al-Zr,Mo and Fe3Al-Zr,Mo,Nb). The addition of small amounts of Zr, Mo or Nb improved the kinetics compar...

Fe3Al intermetallics (Fe3Al, Fe3Al-Zr, Fe3Al-Zr,Mo and Fe3Al-Zr, Mo, Nb) were oxidized at 950 °C in dry and humid (11 vol% water) synthetic air. Thermogravimetric measurements showed that the oxidation rates of the tested intermetallics were lower in humid air than in dry air (especially for Fe3Al-Zr, Mo and Fe3Al-Zr, Mo, Nb). The addition of small amounts of Zr, Mo or Nb improved the kinetics ...