We present a systematic study on the preparation, characteration and potential application of Fe3O4 and Fe3O4@SiO2 nanoparticles. Fe3O4 nanoparticles of controllable diameters were successfully synthesized by solvothermal system with tuning pH. The magnetic properties of nanoparticles were measured by vibration sample magnetometer. Fe3O4@ SiO2 nanoparticles were obtained via classic Stöber proc...

Iron oxide (Fe3O4) nanoparticles have been used in many biomedical approaches. The toxicity of Fe3O4 nanoparticles on mammalian cells was published recently. Though, little is known about the viability of human cells after treatment with Fe3O4 nanoparticles. Herein, we examined the toxicity, production of reactive oxygen species, and invasive capacity after treatment of human dermal fibroblasts...

We demonstrated the effect of superparamagnetic Fe3O4 nanoparticles on Schottky barriers of graphene, in which the Fe3O4 nanoparticles were fabricated by a hydrothermal method and the single-layer graphene sheets were mechanically exfoliated from Kish graphite. The Fe3O4 nanoparticles were superparamagnetic with the saturation magnetic moment of about 32 emu/g at room temperature. We have found...

Acrylic acid and styrene were polymerized onto monodispersed Fe3O4 nanoparticles using a grafting copolymerization method. Aniline molecules were then bonded onto the Fe3O4 nanoparticles by electrostatic self-assembly and further polymerized to obtain uniform polyaniline/Fe3O4 (PANI/Fe3O4) nanoparticles (approximately 35 nm). Finally, monodispersed Ag/PANI/Fe3O4 nanoparticles were prepared by a...

The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified Stöber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were characterized by means of X-ray diffraction (XRD), Raman spectra, scanning electron microscope (SEM) and vibrating sample magnetometer (VSM). Recently, the studies focus on how to im...

The photothermal effect of Fe3O4 magnetic nanoparticles is investigated for cancer therapy both in vitro and in vivo experiments. Heat is found to be rapidly generated by red and near-infrared (NIR) range laser irradiation of Fe3O4 nanoparticles with spherical, hexagonal and wire-like shapes. These Fe3O4 nanoparticles are coated with carboxyl-terminated poly (ethylene glycol)-phospholipid for e...

Chitosan functionalized Fe3O4-Au core shell nanoparticles have been prepared using a two-step wet chemical approach using NaBH4 as reducing agent for formation of Au in ethylene glycol. X-ray diffraction studies shows individual phases of Fe3O4 and Au in the as prepared samples with crystallite size of 5.9 and 11.4 nm respectively. The functionalization of the core-shell nanostructure with Chit...

We report a facile intracellular manipulation of fluorescent magnetic Fe3O4-CdSe nanoparticles using magnetic force. The growth of CdSe quantum dots on Fe3O4 nanoparticles produces Fe3O4-CdSe nanoparticles with two distinct properties, fluorescence and superparamagnetism. After nonspecific surface modification using glutathione (GSH), the hydrophilic Fe3O4-CdSe@GSH nanoparticles can be easily u...

In this article, we proposed a facile one-step synthesis of Fe3O4 nanoparticles of different shapes and sizes by co-precipitation of FeCl2 with piperidine. A careful investigation of TEM micrographs shows that the shape and size of nanoparticles can be tuned by varying the molarity of piperidine. XRD patterns match the standard phase of the spinal structure of Fe3O4 which confirms the formation...

The Fe3O4/CeO2 magnetic photocatalyst was prepared by coating directly onto the surface of magnetic Fe3O4 particles. However a direct contact of CeO2 onto the surface of magnetic Fe3O4 particles presented unfavorable heterojunction, thus the SiO2 barrier layer between magnetic Fe3O4 and CeO2 was prepared as a core-shell stucture to reduce the negative effect by combining three steps of the hydr...