The susceptibility of tin-plated contacts to fretting corrosion is a major limitation for its use in electrical connectors. The present paper evaluates the influence of a variety of factors, such as, fretting amplitude (track length), frequency, temperature, humidity, normal load and current load on the fretting corrosion behaviour of tin-plated contacts. This paper also addresses the developme...

The medical device industry is still seeking answers to the mechanically-assisted corrosion (MAC) problem, which becomes increasingly important due to modularity in design. MAC manifests in various forms, some of which are fretting corrosion, crevice corrosion and stress corrosion. Several studies have been conducted to understand the causes and the factors that affect fretting corrosion. Some ...

BACKGROUND Previous studies regarding modular head-neck taper corrosion were largely based on cobalt chrome (CoCr) alloy femoral heads. Less is known about head-neck taper corrosion with ceramic femoral heads. QUESTIONS/PURPOSES We asked (1) whether ceramic heads resulted in less taper corrosion than CoCr heads; (2) what device and patient factors influence taper fretting corrosion; and (3) w...

This study examines how taper design affects corrosion and fretting at the head trunnion surface. All hip prostheses retrieved between 1999 and 2013 with 28mm/+0 heads were selected, resulting in 44 cobalt-chrome-on-polyethylene implants, representing six taper designs. Mean implantation time: 8.9±3.7years. The femoral head tapers were scored for fretting and corrosion using the Goldberg scale ...

Introduction: Modular head-neck total hip arthroplasty (THA) offers several benefits for orthopaedic surgeons, including intraoperative flexibility and the ability to change the head at revision surgery [1]. However, modularity at the head-neck taper, especially the use of metallic heads and stems, can lead to fretting and corrosion at the taper junction, leading to metal ions and debris releas...

The purpose of this study was to characterize the prevalence of taper damage in modular TKA components. One hundred ninety-eight modular components were revised after 3.9±4.2 years of implantation. Modular components were evaluated for fretting corrosion using a semi-quantitative 4-point scoring system. Design features and patient information were assessed as predictors of fretting corrosion da...

Fretting corrosion is a form of accelerated atmospheric oxidation which occurs at the interface of contacting materials undergoing slight, cyclic relative motion. In electric contacts involving non-noble metals, fretting action can cause rapid increases in contact resistance, proceeding to virtual open circuits in a matter of minutes in the worst cases. Experimental results of resistance increa...

This work aims at investigating experimentally fretting corrosion, that is, corrosion induced by friction of AISI 316L SS against poly(methyl methacrylate) under small displacements, and subsequently using the data to model wear. The observed wear on the stainless steel has been modeled using the Point Defect Model (PDM). The originality of this approach in applying the PDM to fretting corrosio...

Hafnium has been suggested as an interesting material for biomedical applications due to its good biocompatibility and osteogenesis. However, its behaviour under fretting corrosion conditions, found in applications such as dental and joint implants, has not been studied in depth. A three-electrode electrochemical cell integrated with a ball-on-flat reciprocating tribometer was used to investiga...

Experimental cast titanium alloys containing 20 mass% chromium (Ti-20Cr) show preferable mechanical properties and a good corrosion resistance. This study evaluated the fretting corrosion behavior of Ti-20Cr. Ti-20Cr (n = 4) and commercially pure titanium (CP-Ti, n = 6) disk specimens were used. The fretting corrosion test was performed by electrochemical corrosion at 0.3 V in 0.9% saline solut...