OBJECTIVE To assess the shear bond strength of metallic orthodontic brackets bonded with either Fuji Ortho or Ortho Glass LC resin-reinforced glass ionomer cements to enamel surfaces under different conditions, namely, enamel without etching, enamel conditioned with 37% phosphoric acid and enamel conditioned with Transbond Plus Self Etching Primer (TPSEP). MATERIALS AND METHODS One hundred an...

background. acid etching prior to orthodontic bracket bonding may result in enamel wear or cracks following bracket removal. the manufacturer of fuji ortho lc glass-ionomer (gi) claims that it can bond brackets to wet unetched enamel. this study aimed to compare the bracket bond strength to etched and unetched enamel under dry and wet conditions. methods. in this in vitro study, 60 intact premo...

The purpose of the study was to evaluate the shear bond strength of stainless steel orthodontic brackets directly bonded to extracted human premolar teeth. Fifty teeth were randomly divided into five groups: (1) System One (chemically cured composite resin), (2) Light Bond (light-cured composite resin), (3) Vivaglass Cem (self-curing glass ionomer cement), (4) Fuji Ortho LC (light-cured glass i...

Introduction A great number of techniques have been used for bonding orthodontic brackets to the tooth surfaces. Glass ionomer cements are frequently used material for this purpose. The aim of this study was to measure the shear bond strength of orthodontic brackets bonded with glass ionomer cement Ortho Fuji LC and remained adhesive on the enamel surface after brackets debonding. Material and ...

The purpose of this study was to evaluate the shear bond strengths of four light-cured glass ionomer cements used for direct bonding of ceramic brackets, and to compare the results with a two-paste chemically-cured composite resin. Two commercially available polycrystalline ceramic brackets, with either chemically or mechanically retentive bracket bases, were evaluated. The brackets were bonded...

The aim of this study was to test the hypothesis that there is no difference in the fluoride release behavior of resin-reinforced glass ionomer cements before or after fluoride recharge. The materials were divided into 5 groups: 2 resin-reinforced glass ionomer cements used for attaching orthodontic bands, that is, group FOB (Fuji Ortho Band) and group MCB (Multi-Cure Glass Ionomer Orthodontic ...

The purpose of this study was to compare the bond strengths and to evaluate the debonding site using the adhesive remnant index (ARI) provided by a conventional acid-etch conditioner and a new self-etching adhesive system, Xeno IV (Dentsply Caulk). One hundred and eighty bovine lower incisors were randomly divided into six groups (n = 30). In groups 1, 2, and 3, Transbond XT (3M Unitek) composi...

INTRODUCTION For orthodontists, the ideal bonding material should be less moisture-sensitive and should release fluoride, thereby reducing unfavorable iatrogenic decalcification. Resin-Modified Glass Ionomer Cements (RMGICs), due to their ability to bond in the presence of saliva and blood can be a very good bonding agent for orthodontic attachments especially in the areas of mouth, which are d...

The aims of this study were to evaluate the shear bond strength (SBS), fracture mode, and wire pull out (WPO) resistance between resin-modified glass ionomer cement (RMGIC) and conventional orthodontic composite used as a lingual retainer adhesive. Forty lower human incisors were randomly divided into two equal groups. To determine the SBS, either Transbond-LR or Fuji Ortho-LC was applied to th...

adequate bond strength between glass ionomer cements and composite resin is necessary for the success of the sandwich technique.this study assessed the micro-shear bond strength of composite resin to glass-ionomer cements (gic) using self-etch adhesives with different ph values.one hundred specimens (6×4×2 mm) were made using fuji ii and fuji ii lc gics and treated with different adhesives as f...