The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...

Microbial biofilm and corrosion in cooling systems are the most common problems that damage expensive equipment, cause loss of production, and increase maintenance costs. Sulfate reducing bacteria were considered the major bacterial group involved in microbiologically influenced corrosion (MIC). We investigated the survival and enumeration of biofilm-associated SRB on coupons of galvanized stee...

The effect of variety and moisture content on some engineering properties of five improved paddy rice varieties was investigated within moisture content range of 10% and 30% dry basis (d.b.). Increase in moisture content was found to increase the linear dimensions, mass of 100 seeds, surface area, apparent volume, true volume, arithmetic mean diameter, effective geometric diameter, sphericity, ...

A three-dimensional (3D) finite element (FE) model is applied to predict the temperature evolution in the laser welding of galvanized high-strength steels in a zero-gap lap joint configuration. A rotary Gaussian volumetric heat source model is introduced to simulate the laser energy input. The temperature data measured by thermocouples are used to verify the boundary conditions of the thermal m...

Rapid development of automotive industry brings also increased requirements for sheets properties, involving relatively high strength and good formability together with excellent corrosion resistance. Increasing requests for corrosion resistance lead to the production of coated car parts, protected mainly by zinc coatings. Whereas, majority of European producers of passenger cars use preferenti...

With good mechanical properties and corrosion-resistance, galvanized coils are used in many fields nowadays, such as auto industry and household appliance industry. Because of high additional value of galvanized product, steel plants pay much more attention on how to make continuous galvanizing lines (CGL) run efficiently. In this paper, we address a scheduling problem of continuous galvanizing...

In the paper the methodology and test results of field and laboratory corrosion tests of steel earthing rods with zinc galvanized coatings and copperbonded coatings are described. The corrosion rate and level of corrosion damage of earthing rods with two different protective coatings have been compared as well some conclusions related to reliability and assessment of technical “life time” of st...

P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic This review article mainly describes the composition of intermetallic Fe Zn, i.e. zeta (ζ), delta (δ1k + δ1p), gamma1 (Γ1) and gamma (Γ) on galvanized steel during low temperature galvanization (t ~ 450 °C). It gives detail...

P. Pokorný, D. Dobiáš, M. Vokáč – Czech Technical University – Klokner Institute, Prague, Czech Republic This paper evaluates the effect of initial corrosion damage to the surface of the hot dip galvanized steel coating in fresh concrete on its final bond strength. The tests were performed on uncoated and hot-dip galvanized ribbed reinforcements. The measurement of bond stress (τm) according to...

This study is a detailed failure analysis of galvanized high carbon steel wires, which developed coating cracks during the torsion test performed as a quality control at the end of the manufacturing process. Careful visual inspections showed that the cracks are already present in the coating before the torsion test. In order to explain the origin of these cracks, systematic metallographic inves...