In order to obtain a lightweight material having an excellent high-temperature strength, Mg alloy composites reinforced with short alumina fibers and in situ Mg2Si particles were fabricated. The composites were fabricated by pressureless infiltration of the Mg alloy melt into the preform consisting of the fibers and attached Si particles. The volume fraction of Si particles in the preform, the ...

Short alumina fiberand in situ Mg2Si particle reinforced magnesium alloy composites were fabricated by squeeze casting. The in situ Mg2Si particles were formed during the infiltration with the melt into the preforms consisting of the fibers having Si particles attached to their surfaces. The microstructure of the composites and their tensile strength and Young’s modulus in the range from 293K t...

Mg2Si with narrow band gap has attracted increasing interest for its great potential applications. Theoretical calculations have predicted the metallization of Mg2Si under high pressure. In this work, the electrical resistance and Raman spectrum measurements of semiconducting Mg2Si were performed to investigate the metallization of Mg2Si by using diamond anvil cells and strip opposite anvils. A...

New Mg2Si-based multilayer structures were proposed for XRF analysis of the light elements from magnesium to nitrogen. These structures contain two, three or more different layer materials in a single period. The additional third, fourth, etc, layer was introduced for improving performance as well as for application dependent performance flexibility. Three-layer W/SiC/Mg2Si and two layer Co/Mg2...

In this paper, the effect of different alloying elements on the ultimate tensile strength of Al-Mg2Si composites is theoretically studied. The feed forward back propagation neural network with sigmoid function is used. The extensive experimental results taken from literature are modeled and mathematical formula is presented in explicit form. In addition, it is observed that magnesium and copper...

Magnesium silicide (Mg2Si)/carbon nanotube (CNT) thermoelectric nanofibers for use as a flexible thermoelectric material were successfully synthesized through the combined processes of the sol-gel method, magnesiothermic reduction, and liquid-solid phase reaction. In the resulting product, each CNT was coated with Mg2Si which was an approximately 60-nm-thick single crystal. The synthesized Mg2S...

This research was carried out to investigate the influence of Sr–Sb on the microstructures and mechanical properties of Al–18 wt % Mg2Si–4.5Cu alloys. After the addition of 0.2 wt % Sr–Sb, the morphologies of primary Mg2Si transformed from equiaxed dendrite to cube in as-cast alloys and the average size of primary Mg2Si decreased from ~50 to ~20 μm. The shape of eutectic Mg2Si changed from Chin...

It is found that Li2Sb compound can act as the nucleus of primary Mg2Si during solidification, by which the particle size of primary Mg2Si decreased from ~300 to ~15–25 μm. Owing to the synergistic effect of the Li2Sb nucleus and adsorption-poisoning of Li atoms, the effect of complex modification of Li-Sb on primary Mg2Si was better than that of single modification of Li or Sb. When Li-Sb cont...

The role of Mg2Si in the electrochemical behavior of Al-Si-Mg aluminum alloys has been studied using four experimental aluminum alloys with variations in the Si/Mg molar ratio (A1-0.12, A2-0.49, A3-0.89, A4-1.05), in neutral aerated 0.1M NaCl solutions. Accordingly, the corrosion potential in open circuit (Eoc) and polarization resistance (Rp) were measured. Results show that the augment in Si/...

Nine Al-(1-3)Mg-(0-0.4)Cu-0.15Si-0.25Mn (in wt%) alloys with potential applications in both packaging and automotive industries have been investigated. Tensile testing showed that solution strengthening is in good approximation linearly proportional to the Mg content. Mechanical testing and microstructural examinations of aged samples indicate that Mg2Si phase precipitates contribute to age har...