2017
Zixuan Yang Bo Kan Jinxu Li Yanjing Su Lijie Qiao Alex A. Volinsky

Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can decrease the breakdown potential and lead to a reduced transpassivity region. Metastable test re...

2017
Jin-yang Jiang Yao Liu Hong-yan Chu Danqian Wang Han Ma Wei Sun

In this study, the pitting behaviour of a new corrosion-resistant alloy steel (CR) is compared to that of low-carbon steel (LC) in a simulated concrete pore solution with a chloride concentration of 5 mol/L. The electrochemical behaviour of the bars was characterised using linear polarisation resistance (LPR) and electrochemical impedance spectroscopy (EIS). The pitting profiles were detected b...

2010
G. S. Frankel

Pitting corrosion is localized accelerated dissolution of metal that occurs as a result of a breakdown of the otherwise protective passive film on the metal surface. This paper provides an overview of the critical factors influencing the pitting corrosion of metals. The phenomenology of pitting corrosion is discussed, including the effects of alloy composition, environment, potential, and tempe...

2016
Shozaburo Yanamoto Jiro Fukae Yurie Fukiyama Shinsuke Fujioka Shinji Ouma Yoshio Tsuboi

BACKGROUND Remitting seronegative symmetrical synovitis with pitting edema syndrome is characterized by symmetrical synovitis with pitting edema in the dorsum of the hands or feet. Most cases of remitting seronegative symmetrical synovitis with pitting edema syndrome are idiopathic, but some are secondary to malignancy, autoimmune disease, or neurodegenerative disorders. Pleural and pericardial...

Journal: :Cases Journal 2008
Abdul Salam Rafik Henry Tom Sheeran

Remitting Seronegative Symmetrical Synovitis with Pitting oedema syndrome, a rare inflammatory arthritis, commonly affects people in the older age group. It can present as an acute onset polyarthritis with associated pitting oedema of the extremities. Patients show excellent response to low dose steroids with complete and sustained remissions. It can also be a paraneoplastic manifestation of an...

2013
Zhifei Wu Tie Wang Ruiliang Zhang

There were severe pitting corrosions on the surface of transmission gears in diesels. The cause of metal fatigue pitting of gear surface is analyzed in the paper, which based on the contact fatigue experiment of 18Cr2Ni4WA carburizing and quenching gears used in the diesel engine. Causes of pitting on harden tooth surface are studied from three aspects: gear surface residual stress field, oil f...

2008
Wei LI Guang DAI Feifei LONG Peng JIANG

According to the characteristics of low-carbon steel pitting acoustic emission signal, one new characteristic analysis-WICA is proposed. The main idea of WICA is that based on the independent component analysis blind source separation technology as well as the wavelet transformation decomposition technology, proposed determines the low-carbon steel pitting source number according to the energy ...

2005
Caroline Kimmy Nguyen

Interactions between copper and chlorine disinfectants were examined from the perspective of disinfectant decay and copper pitting corrosion. Sparingly soluble cupric hydroxide catalyzed the rapid decay of free chlorine, which in turn, led to production of less soluble and more crystalline phases of cupric hydroxide. The catalytic activity of the cupric hydroxide was retained over multiple cycl...

2005
K. Srinivasa K. Prasad

This review attempts to present the current understanding of the mechanism of pitting corrosion of heat treatable aluminium alloys and their welds. The role of alloying elements and intermetallic phases on the corrosion behavior of these alloys has been discussed. Pitting mechanism of aluminiumcopper alloys is specifically discussed. Finally effect of welding on the pitting corrosion of these a...

2014
Tingyue Gu

Biocorrosion, also known as microbiologically influenced corrosion (MIC), is caused by various corrosive biofilms. So far, laboratory experimental MIC pitting tests in the published literature have overwhelmingly focused on sulfate reducing bacteria (SRB) that use sulfate as the terminal electron acceptor because SRB and sulfate are often found at anaerobic pitting sites. Many laboratory pure-c...