in this study , the physical and mechanical properties of polypropylene composites reinforced with bagasse alkaline-sulfite-anthraquinone, soda-anthraqouinone, monoethanolamine-anthraquinone chemical pulps and mechanical pulp (cmp) known as pulp-plastic compostes (ppc) were investigated and the results were compared among ppcs and with polypropylene composites reinforced with bagasse flour know...

Potassium methyl siliconate (PMS) was investigated as a new nano modifier of wood fiber and wood flour to improve the compatibility between the fiber/flour and the plastic matrix in fiber reinforced plastic composites. Before injection molding, bleached and brown pulp fibers and mixed species wood flour were pretreated in PMS solutions. The morphology of the treated and untreated fiber and flou...

Polypropylene/wood flour composites were melting compounded in an internal mixer at 190°C and 60 rpm rotor speed and then samples were fabricated by injection molding. Effects wood flour content on the physical properties of composites was investigated. For this purpose, hardness, water absorption and thickness swelling of samples was determined at different levels of wood flour content. The re...

In this work, post-consumer polypropylene and wood flour from Pinus elliottii were used to produce wood plastic composites. The effect of polypropylene grafted with itaconic acid used as a coupling agent on mechanical properties, thermal stability and morphology of the composites was investigated and compared with the composite developed with polypropylene grafted with maleic anhydride, commonl...

the creep/recovery behavior of wood flour-polypropylene was compared with medium density fiberboard (mdf) and particleboard. for this purpose, wood flour-polypropylene composites (with and without compatibilizer)were manufactured by using a laboratory twin-screw extruder. the mdf and particleboard panels were obtained from local producers. short term flexural creep tests at 30% of ultimate bend...

In this work, the potential for usage recycled polystyrene and wood flour wastes as materials for development wood plastic composites was evaluated. The effects of wood flour loading and coupling agent addition on the mechanical, dynamic mechanical and morphological properties of polystyrene wood flour composites were examined. The results showed that the mechanical properties decreased with th...

Though silane chemistry has been used to crosslink unfilled polyethylene for many years, such crosslinking has only been recently applied to wood plastic composites to improve properties such as creep resistance. However, the presence of wood significantly changes the silane chemistry and a greater understanding is necessary for optimal processing and performance. We investigated three differen...

In this work, the influence of three types of styrene maleic anhydride (SMA) oligomers on the adhesion of polystyrene wood plastic composites (WPC) was investigated. The composites were processed on a twin-screw co-rotating extruder below 200°C using 20 wt% of wood flour. The styrene maleic anhydride with different content of maleic anhydride groups, 30%, 25% and 20% (w/w) and levels of 1, 2 an...

To illustrate the effects of nano-bamboo charcoal (NBC) on the properties of bamboo plastic composites (BPC), nano-bamboo charcoalbamboo plastic composites (NBC-BPC) were prepared at 0%, 2.5%, 5%, 7.5%, 10%, and 12.5% (w/v) NBC and characterized. The effects of NBC on the water absorption, fractured surfaces, mechanical properties, and thermal properties of the composites were investigated. NBC...

hemicellulose of southern yellow pine wood spices was extracted by pressurized hot water at three different temperatures: 140°c, 155°c and 170°c. compounding with pp (polypropylene) was performed by extrusion after preparing wood flour and sieving to determine its mesh size. the ratio of wood to polymer was 50:50 based on oven-dry weight of wood flour. all extraction treatments and control samp...