Conventional and new sintering mechanisms have been porous compacts is well-known in the ceramic literature. However, several reports have been presented recently that investigated using fine powders of CeO2 and Y2O3 of excellent sinterability. We have verified the validity of Herring’s show that particle/grain size can remain essentially constant up to a density of 92%, and such a resistance t...
Shrinkage behavior and crack formation during firing have been investigated for Al2O3/Ce-TZP composites that have been fabricated by colloidal rolling and folding. These composites show improved sinterability and sinter isotropically after repeated rolling. Interface instability in rolling creates corrugated interfaces with large layer waviness; therefore, rolling can substantially alleviate th...
The sinterability, microstructure, and mechanical properties of pure TiB2- CrB2-doped ZrB2 prepared by spark plasma sintering were investigated. solid solutions synthesized the complete borothermal reduction to form (Zr0.95Ti0.05)B2 (Zr0.95Cr0.05)B2. results showed that solution yielded smaller particle size than sinterability was also improved with use solutions, as evidenced an increase relat...
Using intermediate, liquid-forming compositions in the approach focuses on the Si3N4–R2O3 binary, where R2O3 is any (Y,La)2O3–AlN system as additives, fully dense Si3N4 ceramrare-earth oxide (or Y2O3) used singly or severally. After sinics with high strength at high temperature have been tering, this composition forms -Si3N4 and some refractory rareobtained by pressureless sintering. The cerami...
Vanadium carbonitrides (VCxN1-x) were prepared via mechanosynthesis from mixtures of elemental vanadium and carbon with different V/C atomic ratios under a nitrogen atmosphere using a high-energy ball mill. We obtained the full composition range of carbonitrides at room temperature. The products were characterized using X-ray diffraction, scanning electron microscopy and electron energy loss sp...
In the present work, Al2O3-CeO2 composite nanopowders were synthesized via co-precipitation method. The sinterability of the synthesized powders was investigated. The results showed that the transformation of transition phases of alumina to α-Al2O3 takes place at 1200 °C. TEM images showed that the powders was composed of nanoparticles in the range of 30−70 nm. The densification of composites s...
The effect of high-frequency (HF) electric fields on the crystallization and sintering rates of a lithium aluminum germanium phosphate (LAGP) ion conducting ceramic was investigated. LAGP with the nominal composition Li1.5Al0.5Ge1.5(PO4)3 was crystallized and sintered, both conventionally and under effect of electrical field. Electrical field application, of 300 V/cm at 1 MHz, produced up to a ...