BACKGROUND This study aimed to compare superelastic and heat-activated nickel-titanium orthodontic wires' surface morphology and potential release of nickel ions following exposure to oral environment conditions. METHODS Twenty-four 20-mm-length distal cuts of superelastic (NiTi Force I®) and 24 20-mm-length distal cuts of heat-activated (Therma-Ti Lite®) nickel-titanium wires (American Ortho...

OBJECTIVE To determine the mechanical properties of commercially available thermodynamic wires and to classify these wires mathematically into different groups. MATERIALS AND METHODS The samples examined were 48 nickel-titanium (NiTi) alloy orthodontic wires commercially available from five manufacturers. These samples included 0.016-inch, 0.016- x 0.022-inch, 0.017- x 0.025-inch, and 0.018- ...

BACKGROUND The initial arch wire is the first arch wire to be inserted into the fixed appliance at the beginning of orthodontic treatment and is used mainly for correcting crowding and rotations of teeth. With a number of orthodontic arch wires available for initial tooth alignment, it is important to understand which wire is most efficient, as well as which wires cause the least amount of root...

most published results about the characteristics of niti wires are based on the mechanical laboratory tests on the as-received wires.the purpose of this study was to investigate the effect of saliva on load-deflection characteristics of superelastic niti wires.in this experimental study, 15 wires of three kinds of superelastic niti wires (sentalloy, force i and truflex) were prepared. five spec...

OBJECTIVE The aim was to evaluate the alteration of the deactivation forces of the most commonly used nickel-titanium wires under long-lasting oral cavity environmental influence. MATERIALS AND METHODS Randomized in vitro and in vivo trials of 540 pieces of orthodontic archwires, NeoSentalloy®, Copper NiTi® 35°C and Titanol Superelastic(®), round (0.016 inch), and rectangular (0.016 × 0.022 i...

OBJECTIVE This research aimed at comparing the qualitative chemical compositions and the surface morphology of fracture regions of eight types of Nickel/Titanium (NiTi) conventional wires, superelastic and heat-activated (GAC, TP, Ormco, Masel, Morelli and Unitek), to the wires with addition of copper (CuNiTi 27ºC and 35ºC, Ormco) after traction test. METHODS The analyses were performed in a ...

The shape memory nickel-titanium alloy has been applied in many fields due to its unique thermal and mechanical performance. One of the successful applications of NiTi wires is in orthodontics because of its good characteristics such as low stiffness, high spring back, high stored energy, biocompatibility, superelasticity and shape memory effect. The mechanical properties of wires are paid spec...

When NiTi powder compacts containing Nb wires are heated above 1 170 8C, each Nb wire reacts with adjacent NiTi powders to form a eutectic liquid which wicks into the space between the remaining NiTi powders. This creates a macropore at the location of the Nb wire while eliminating the microporosity between NiTi powders which is filled with a NiTi/Nb eutectic phase after solidification. This no...

OBJECTIVE Most published results about the characteristics of NiTi wires are based on the mechanical laboratory tests on the as-received wires.The purpose of this study was to investigate the effect of saliva on load-deflection characteristics of superelastic NiTi wires. MATERIALS AND METHODS In this experimental study, 15 wires of three kinds of superelastic NiTi wires (Sentalloy, Force I an...

The effects of the presence of the R-phase in a near-equiatomic NiTi alloy on the mechanical responses of an endodontic instrument were studied by using finite element analysis. The input data for the constitutive model in the simulation were obtained by tensile testing of three NiTi wires: superelastic austenite NiTi, austenite + R-phase NiTi, and fully R-phased NiTi. The wires were also chara...