MCM-41 was used as a support and, by using atomic layer deposition (ALD) in the liquid phase, a catalyst was prepared by consecutively loading titanium oxide and vanadium oxide to the support. This research analyzes the effect of the loading amount of vanadium oxide on the acidic characteristics and catalytic performance in the dehydration of butanol. The physical and chemical characteristics o...

The catalytic performance of incorporated V-MCM-41 catalysts for the partial direct oxidation of methane to formaldehyde with molecular oxygen has been investigated. V-MCM-41 catalysts containing 0.56–1.86 wt.% V have been prepared by incorporating the vanadium ions into the framework of mesoporous siliceous MCM-41, resulting in a highly ordered structure with large BET surface area and high su...

The chromium/vanadium bimetallic Phillips catalysts developed by our research group have been proved to be a promising process to produce bimodal polyethylene using a single-reactor process. The vanadium loading of CrV-1/1, CrV-1/2, and CrV-1/3 has a significant effect on the polymerization activity, product molecular weight (MW), as well as th...

Vanadium oxide grafted on mesoporous silica SBA-15 has been synthesized using a controlled grafting process. Its structure has been thoroughly investigated using different characterization techniques, including N2-physisorption, X-ray diffraction, transmission electron microscopy (TEM), Raman spectroscopy, H2 temperature-programmed reduction, X-ray absorption near-edge structure (XANES), and ex...

With regard to the application in a microstructured reactor, a special VOx/Al2O3 catalyst powder (3 μm) was prepared and characterised by BET, XRD, UV/Vis DRS, and Raman spectroscopy. The higher the vanadium content, the higher the degree of polymerisation of the vanadium species on the support surface and the lower the BET surface area. Pelletised powders were tested in conventional tubular re...

A combined technique of an imaging plate (IP) and thin absorbers was applied to tritium in nickel and vanadium specimens using copper, aluminum, and gold foil as the absorber. Copper and aluminum foil are used as a K-edge filter with X-ray absorption at 9.0 keV and 1.56 keV, respectively. Gold has L-edges X-ray absorption at around 13 keV. With this technique, photostimulated luminescence (PSL)...

Bone and cartilage regeneration can be improved by designing a functionalized biomaterial that includes bioactive drugs in a biocompatible and biodegradable scaffold. Based on our previous studies, we designed a vanadium-loaded collagen scaffold for osteochondral tissue engineering. Collagen-vanadium loaded scaffolds were characterized by SEM, FTIR, and permeability studies. Rat bone marrow pro...

vanadium phosphorus oxides (vpo) has been applied as a heterogeneous catalyst in gas phase oxidation reactions and its application is very limited in liquid phase. in this study a series of cobalt-doped vanadium phosphorus oxides (vpo-co) catalysts with different loading of co (0.01-1.0 mol ratio of co/v) were prepared. oxidation of benzyl alcohol was studied in the liquid phase over vpo and vp...

M2O3–TiO2 (M = Ga, In and La) composite oxides were prepared by a co-precipitation method with in situ generated ammonium hydroxide and were impregnated with 12 wt.% V2O5. The M2O3-TiO2 and V2O5/M2O3-TiO2 (M = Ga, In and La) samples were subjected to thermal treatments from 773 to 1073 K and were investigated by X-ray diffraction, FT-infrared, and BET surface area methods to establish the effec...

The partial oxidation of methanol to formaldehyde was studied over highly dispersed vanadia supported on mesoporous silica SBA-15 (VOx/SBA-15). VOx/SBA-15 catalysts were prepared by a novel grafting/ion-exchange method and characterized using UV-VISand Raman spectroscopy. The resulting surface vanadium oxide species (0 – 2.3 V/nm), grafted on the inner pores of the SBA-15 silica matrix, consist...