Lanthanum substituted Ni-Zn ferrite nanoparticles (Ni0.5Zn0.5LaxFe1-xO4; 0.00 ≤x≤ 1.00) synthesized by sol-gel method were presented. X-ray diffraction patterns reveal the typical single phase spinel cubic ferrite structure, with the traces of secondary phase for lanthanum substituted nanocrystals. In addition, the structural analysis also demonstrates that the average crystallite size varied i...

BACKGROUND During liquid-phase synthesis of γ-Fe2O3 nanoparticles by chemically induced transition in FeCl2 solution, enhancement of surface modification by adding ZnCl2 was attempted by using NaOH. By using transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, energy-dispersive X-ray spectrometry, and vibrating sample magnetometry, the dependence of the synthes...

In this research nickel zinc ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °C for 5 hours. The structure of nanoparticles was studied using X-ray diffraction pattern. The lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticl...

manganese zinc ferrite nanoparticles (mzf nps) were synthesized by using a direct, efficient and environmental friendly hydrothermal method. to improve the colloidal stability of mzf nps for biomedical applications, nps were coated with chitosan by ionic gelation technique using sodium tripolyphosphate (tpp) as crosslinker. the synthesized nps were characterized by x ray diffraction (xrd) analy...

This study was conducted to examine the synthesis of ZnFe2O4 nanoparticles, using the hydroethanolic extract of Citrus aurantium flowers, through the application of FeCl2.4H2O, FeCl3.6H2O, and Zinc Acetate. The present piece of work is regarded important especially when ascertaining the potential of a widely distributed underused mangrove associated plant, C. aurantium, as used in the folk medi...

Introduction Magnetic oxide nanomaterials, including iron oxide (Fe3O4 and γ-Fe2O3), spinel ferrites (MFe2O4; M=Mn, Zn, Cr, Ni, or Co) and hexagonal ferrite (MFe12O19, M=Ba and Sr) are attracting much attention due to their wide application potentials in advanced magnets, electronic devices, information storage, magnetic resonance imaging (MRI), and drug-delivery technology [1-6]. Hence, the sy...

Co-Zn ferrite and BaM ferrite films were deposited on silicon wafer disks with thermally oxidized surface layer without annealing process, and their readlwrite characteristics in contact mode have been investigated by using a MIG and Mn-Zn ferrite head with gap length of 0.2-0.4 pm. The highest linear recording density D50 of Co-Zn ferrite and Ba ferrite films were 105 and 190 WRPI, respectivel...

Manganese-zinc-ferrite nanoparticles (Mn(0.5)Zn(0.5)Fe(2)O(4), MZF-NPs) prepared by an improved co-precipitation method and were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD) and energy dispersive spectrometry (EDS). Then thermodynamic testing of various doses of MZF-NPs was performed in vitro. The cytotoxicity of the Mn(0.5)Zn(0.5)Fe(2)O(4) nanoparticles in v...

The reaction mechanism for conversion of MnO nanoparticles to Mn-ferrite nanoparticles was studied, which involved sequential consumption of MnO and the growth of ferrite. The method could be applied to other ferrite nanoparticles including cobalt ferrite.

The influence of various cations ranging from alkali metals to transition metals according to the periodic table were discussed. The ferrites used were Ni ferrite, Mg ferrite and Zn ferrite having different cation distributions in the spinel lattice. Cations having appropriate ionic radii and valencies are soluble in ferrite. Several additives formed other phase in addition to the spinel phase....