PVP-Assisted Synthesis of Cobalt Ferrite (CoFe2O4) Nanorods

نویسندگان

  • Majid Farahmandjou Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran
  • Saeid Behrouzinia
  • Sarvin Honarbakhsh
چکیده مقاله:

Cobalt ferrite (CoFe2O4) nanorods were synthesized by iron chloride (FeCl3.6H2O) and cobalt sulfate hexahydrate (CoSO4.7H2O) as precursor in the presence of ethylene glycol agent and poly vinyl pyrrolidone (PVP) surfactant. The samples were characterized to identify the physical properties. XRD pattern of cobalt ferrite samples showed the structure of body center cubic (bcc) structure. The diameter of as-prepared samples was determined about 20 nm and annealed one was about 30 and 50 nm in diameter at 500 °C and 1100 °C, respectively. The TEM studies showed that the particles change from rod shaped to sphere-liked shaped particles by increasing annealing temperature. Peaks in the FTIRspectrum determined the element of Fe-Co nanoparticles. EDS shows peaks of iron and cobalt with fewer impurities in prepared samples and Fe/Co ratio was also decreased with increasing annealing temperature. The result of magnetic measurements showed saturation magnetization around 59.5 emu g-1 for annealed samples.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

pvp-assisted synthesis of cobalt ferrite (cofe2o4) nanorods

cobalt ferrite (cofe2o4) nanorods were synthesized by iron chloride (fecl3.6h2o) and cobalt sulfate hexahydrate (coso4.7h2o) as precursor in the presence of ethylene glycol agent and poly vinyl pyrrolidone (pvp) surfactant. the samples were characterized to identify the physical properties. xrd pattern of cobalt ferrite samples showed the structure of body center cubic (bcc) structure. the diam...

متن کامل

Hydrothermal synthesis of nitrogen doped graphene supported cobalt ferrite (NG@CoFe2O4) as photocatalyst for the methylene blue dye degradation

A magnetic NG@CoFe2O4 photocatalyst was developed via a facile hydrothermal method and characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), and vibrating sample magnetometry (VSM) techniques. The CoFe2O4 nanoparticles were found to have a size between 100-150 nm and were unifo...

متن کامل

PLD-assisted VLS growth of aligned ferrite nanorods, nanowires, and nanobelts-synthesis, and properties.

We report here a systematic synthesis and characterization of aligned alpha-Fe2O3 (hematite), epsilon-Fe2O3, and Fe3O4 (magnetite) nanorods, nanobelts, and nanowires on alumina substrates using a pulsed laser deposition (PLD) method. The presence of spherical gold catalyst particles at the tips of the nanostructures indicates selective growth via the vapor-liquid-solid (VLS) mechanism. Through ...

متن کامل

Synthesis and characterization of Ag doped Cobalt Ferrite nanocomposite

Nanomaterials are attracted a great deal of attention from scientific community due to its unique properties and applications. The small size ferrites have opened the door for intensive research to utilize their properties for biomedical applications. Cobalt ferrite nanomaterials and its silver doped (Ag-doped) nanocomposites have been prepared using solid state combustion method. This combusti...

متن کامل

Salt-assisted combustion synthesis of cobalt ferrite nanoparticles; magnetic properties and cation distribution measurement by XRD analysis

Current study represents the effect of the size and synthesis method on the cation distribution of cobalt ferrite nanoparticles and on the magnetic properties. The nanoferrites have been synthesized through sol-gel auto-combustion method using metal nitrates as precursor and citrate as fuel. In order to obtain the fine and agglomerated-free particles, we have used salt-assisted combustion react...

متن کامل

Ultrasonic-assisted solvothermal synthesis of self-assembled Copper Ferrite nanoparticles

The aim of this work was to characterize copper ferrite nanoparticles synthesized via solvothermal method and to investigate the effects of ultrasonic waves on the synthesis efficiency. Crystal structure, functional groups, microstructure, particle size, magnetic properties, specific surface area, porosity distribution and photocatalytic activity of the synthesized nanoparticles were also inves...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 4  شماره 4

صفحات  655- 662

تاریخ انتشار 2016-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023